Blue–white–orange Color-Tunable Luminescence of Ce3+/Mn2+-codoped NaCaBO3via Energy Transfer: Potential Single-Phase White-Light-emitting Phosphors

Jianfeng Sun,Zhipeng Lian,Guangqiu Shen,Dezhong Shen
DOI: https://doi.org/10.1039/c3ra42554a
IF: 4.036
2013-01-01
RSC Advances
Abstract:Ce3+/Mn2+-codoped NaCaBO3 single-phase color-tunable phosphors were synthesized by solid-state reaction, and their photoluminescence properties were investigated in detail. Under UV excitation, two main emission bands peaking at 400 and 610 nm were realized in the NaCa0.89BO3: 0.01Ce(3+), 0.10Mn(2+) phosphor on the basis of the energy transfer from Ce3+ to Mn2+ with an efficiency of over 83%. The energy transfer was validated and demonstrated to be a resonant type via a dipole-dipole mechanism, and the critical distance R-C values calculated by the quenching concentration method and the spectral overlap method were 22.85 and 19.41 angstrom, respectively. On examining the Mn2+-concentration-dependent photoluminescence properties, it was observed that the emission color could be tuned from blue (0.162, 0.031) to white-light (0.335, 0.259) and eventually to orange (0.489, 0.246) through energy transfer by changing the Ce3+/Mn2+ ratio. Combining a 370 nm UV chip and a single-phase white-emitting NaCa(0.9)6BO3(:) 0.01Ce(3+), 0.03Mn(2+) phosphor produced a white light-emitting diode with CIE chromaticity coordinates of (0.326, 0.274) and an excellent color rendering index of 90.7 at a correlated color temperature of 4046 K. These results indicate that the NaCaBO3: Ce3+, Mn2+ phosphors have potential applications as single-phase white-light-emitting phosphor-converted materials for UV-pumped light-emitting diodes.
What problem does this paper attempt to address?