Abstract:Dielectric measurements are reported as a function of temperature for phase transformations in the lead magnesium niobate-lead titanate system (PMN-PT). Data are given for single crystal specimens in the morphotropic phase boundary (MPB) region. Transition temperatures were determined from dielectric loss data. The characteristics for both poled and unpoled crystals are compared. Values of dielectric constant were found to increase after poling at room temperature, and an anomaly was induced at the lower-temperature transition. Details are reported for these properties depending upon composition within the MPB region. At room temperature, the poled crystals had high values for dielectric constant (e.g., 5000–15 000), piezoelectric coefficient (e.g., 1000–4000pC∕N), and electromechanical coupling factor (e.g., >0.9). The temperature dependence of dielectric properties is treated in terms of competing phases at transformations, with a change from continuous to discontinuous behavior with increasing PT content towards the MPB. The effect of poling on the induction of the tetragonal (T) phase, with a lowering of the low temperature to tetragonal (LT→T) phase transformation temperature, is discussed. Piezoelectric crystals with the highest depoling temperature were farthest away from the MPB in the MPB region. This information should be useful for the application of PMN-PT piezoelectric crystals.

Evidence of Macro–micro Domain Transition in Poled PMN–PZT Ceramics

Investigation on Microscopic Mechanisms of High-Curie Temperature PMN-PH-PT Piezoelectric Ceramics

Microstructures And Pyroelectric Properties Of Multicomposition 0.9pbzro(3)Center Dot Xpbtio(3)Center Dot(0.1-X)Pb(Zn1/3nb2/3)O-3 Ceramics

Microstructures and Pyroelectric Properties of Multicomposition 0.9PbZrO<sub>3</sub>·<i>x</i>PbTiO<sub>3</sub>·(0.1−<i>x</i>)Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>Ceramics

Relaxor Ferroelectric Characteristics And Temperature-Dependent Domain Structure In A (110)-Cut (Pbmg1/3nb2/3o3)(0.75)(Pbtio3)(0.25) Single Crystal

Ferroelectric 90° Domain Evaluation in Tetragonal Pb(Mg1/3Nb2/3)O3–PbTiO3 Ceramics

Effect of PMN Content on the Phase Structure and Electrical Properties of PMN–PZT Ceramics

Field Induced O-MC Phase Transition and Domain Structure Evolution in Pb(Mg1/3Nb2/3)O3-0.34PbTiO3 Single Crystals under Radial Poling

Structural Phase Transition Behaviour And Electrical Properties Of Pb(Mg1/3nb2/3)O-3-Pbtio3-Pbzro3 Ceramics

Composition and Temperature Dependence of Ferroelectric and Pyroelectric Properties of (1 − X )[PMN–PT(65/35)]– X PZ (0 ≤ X ≤ 0.10) Ceramics

Domain Structure and Evolution in ZnO‐modified Pb(Mg1/3Nb2/3)O3–0.32PbTiO3 Ceramics

Temperature-Dependent Ferroelectric Dynamic Hysteresis Properties of Modified Pmn-Pzt Relaxor Ceramics

Microstructure and Dielectric Properties of PZN-PT-BT Relaxor Ferroelectric Ceramics

Domain Morphology Evolution Associated with the Relaxor–normal Ferroelectric Transition in the Bi- and Zn-modified Pb(Ni1/3Nb2/3)O3–PbZrO3–PbTiO3 System

Reorientation of Defect Dipoles in Ferroelectric Ceramics

Domain Switching and Microcracking During Poling of Lead Zirconate Titanate Ceramics

Morphotropic Phase Boundary and Electrical Properties of PMN-PZN-PT Ceramics

Dielectric Relaxation Behavior of Ceramics in the Pb(Zn 1/3 Nb 2/3 )O 3 -Batio 3 -Pbtio 3 System

Microstructure Basis for Strong Piezoelectricity in Pb-free Ba(Zr0.2Ti0.8)O3-(Ba0.7Ca0.3)TiO3 Ceramics

Effect of poling on dielectric anomalies at phase transitions for lead magnesium niobate-lead titanate crystals in the morphotropic phase boundary region

Microstructure and Electromechanical Properties in Pmnn-Pzt Ceramics Sintered at Different Temperatures