In-situ Interfacial Polymerization of Polyamide TFN Membranes by Adding a Diamino-Silane Coupling Agent: Toward Enhanced Desalination Performance
Huanhuan Wu,Qian Zhang,Bing Xu,Xin Liu,Yakai Lin,Nan Jiang,Hong Yao,Yuanhui Tang,Lin Wang,Lixin Yu,Zhenzhong Yang,Xiaolin Wang
DOI: https://doi.org/10.1016/j.desal.2024.117508
IF: 11.211
2024-01-01
Desalination
Abstract:The primary challenge faced by thin film nanocomposite (TFN) membrane in nanofiltration (NF) process is to effectively resolve the trade-off effect between permeability and selectivity. Herein, a polyamide (PA) TFN membrane with enhanced NF performance was prepared through in -situ interfacial polymerization (in -situ IP) method, using piperazine (PIP) and 3-diamino-methyl-cyclohexyl triethoxysilane (DTES) as co-amine monomers to undergo a reaction with 1,3,5-benzenetricarbonyl trichloride (TMC). This study investigated the effects of DTES on the surface chemical composition, morphologies, hydrophilicity, separation efficiency, and anti-fouling properties of the novel DTES/PIP/TMC TFN membranes. It was found that SiO 2 nanoparticles were generated insitu from the reacted DTES through hydrolysis and self -condensation, resulting in their uniform distribution within the formed PA selective layer with high compatibility and without aggregation. The optimal PA TFN membrane was achieved by adjusting the ration of Si -OH group in formed SiO 2 nanoparticles through varying the concentration of DTES concentration. Meanwhile, the induction of SiO 2 into the PA layer resulted in an enlargement in membrane pore size and improved surface hydrophilicity. When the concentration of added DTES was 0.333 wt%, the optimal PA TFN membrane (TFN-4) exhibited the highest quantity of formed Si -OH groups, resulting in the excellent performance, including a markedly enhanced water permeability flux of 76.8 L & sdot; m - 2 & sdot; h - 1 (2-fold larger than that of the pure TFC membrane), a great Na 2 SO 4 rejection of 97.5 %, and a superior Cl - /SO 4 2- permeation selectivity of 46.0. Moreover, the TFN-4 membrane exhibited exceptional stability and superior antifouling properties attributed to its unparalleled hydrophilicity. This work provided a strategy for preparing uniform and high-performance TFN membranes.