Manipulating Cu Nanoparticle Surface Oxidation States Tunes Catalytic Selectivity Toward CH4 or C2+ Products in CO2 Electroreduction
Qikui Fan,Xue Zhang,Xiaohu Ge,Licheng Bai,Dongsheng He,Yunteng Qu,Chuncai Kong,Jinglei Bi,Dawei Ding,Yueqiang Cao,Xuezhi Duan,Jin Wang,Jian Yang,Yuen Wu
DOI: https://doi.org/10.1002/aenm.202101424
IF: 27.8
2021-01-01
Advanced Energy Materials
Abstract:Herein, a facile seed-assisted strategy for preparing Cu nanoparticles (NPs) with polyvinyl pyrrolidone (PVP) capping is presented. Compared to the Cu NPs with deficient PVP protection, the Cu NPs capped with a sufficient amount of PVP remain almost completely as Cu-0 species. In contrast, the Cu NPs that are considered PVP deficient form an oxide structure in which the inner layer is face-centered cubic Cu and the outer layer is, at least in part, made up of Cu2O species. Furthermore, to eliminate CO2 molecule diffusion and simultaneously obtain significant current density (200 mA cm(-2)) for industrial applications, a flow cell configuration is used for carbon dioxide electro reduction reaction (CO2RR) testing in 0.5 m potassium hydroxide solution. The Cu NPs with zero valence deliver Faradaic efficiencies (FEs) for the CO2 reduction to CH4 of over 70%, with a current density exceeding 200 mA cm(-2), outstripping the performances of the majority of the reported CO2 electrocatalysts. Interestingly, the distribution of products catalyzed by the Cu NPs with +1 valence includes multicarbon products (C2+) such as C2H4, C2H5OH, CH3COOH, and C3H7OH with combined FEs of >80%, with current densities of up to 300 mA cm(-2). The above results unambiguously establish that surface oxidation of Cu species plays a crucial role in the CO2RR.