Abstract:Sulfate-reducing bacteria (SRB) can regulate environmental pH because of their metabolism. Because local acidification results in pitting corrosion, the potential capacity of pH regulation by SRB would have important consequences for electrochemical aspects of the bio-corrosion process. This study focused on identifying the effect of pH on the corrosion of duplex stainless steel 2205 in a nutrient-rich artificial seawater medium containing SRB species, Desulfovibrio vulgaris . Duplex stainless steel samples were exposed to the medium for 13 days at 37°C at pH ranging from 4.0 to 7.4. The open-circuit potential value, sulfide level, pH and number of bacteria in the medium were recorded daily. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization were used to study the properties of the biofilms at the end of the experiments and the corrosion behaviour of the material. Inductively coupled plasma mass spectrometry was used to measure the concentration of cations Fe, Ni, Mo, Mn, Cr in the experimental solution after 13 days. Scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDX) were used for surface analysis. The results showed the pH changed from acidic values set at the beginning of the experiment to approximately pH 7.5 after 5 days owing to bacterial metabolism. After 13 days, the highest iron concentration was in the solution that was initially at pH 4 accompanied by pitting on the stainless steel. Sulfur was present on all specimens but with more sulfur at pH 4 in the EDX spectra. EIS showed the film resistance of the specimen at pH 4 was much lower than at pH 7.4 which suggests the corrosion resistance of the stainless steel was better at higher pH. The results of this study suggest that the corrosion process for the first few days exposure at low pH was driven by pH in solution rather than by bacteria. The increasing pH during the course of the experiment slowed down the corrosion process of materials originally at low pH. The nature and mechanism of SRB attack on duplex stainless steel at different acidic environments are discussed.

Surface Chemistry and Corrosion Behaviour of 304 Stainless Steel in Simulated Seawater Containing Inorganic Sulphide and Sulphate-Reducing Bacteria

A Comparative Study of Corrosion of 316L Stainless Steel in Biotic and Abiotic Sulfide Environments

Characteristics of Sulfide Corrosion Products on 316L Stainless Steel Surfaces in the Presence of Sulfate-Reducing Bacteria

Effects of Sulphate-reducing Bacteria on Corrosion Behaviour of 2205 Duplex Stainless Steel

Localized Corrosion Behavior of 316L Stainless Steel in the Presence of Sulfate-Reducing and Iron-Oxidizing Bacteria

Corrosion Behavior of 316L Stainless Steel in the Combination Action of Sulfate-Reducing and Iron-Oxidizing Bacterias

Synergistic effect between sulfate-reducing bacteria and Shewanella algae on corrosion behavior of 321 stainless steel

Influence of Sulfate-reducing Bacteria in Circulating Cooling Water on Corrosion Behavior of Stainless Steel

The influence of sulphate‐reducing bacteria on heterogeneous electrochemical corrosion behavior of Q235 carbon steel in seawater

A study of bacteria adhesion and microbial corrosion on different stainless steels in environment containing Desulfovibrio vulgaris

Effect of Sulphate Reducing Bacteria on Corrosion of AlZnInSn Sacrificial Anodes in Marine Sediment

Corrosion Behavior of Copper under Biofilm of Sulfate-Reducing Bacteria

Effect of One Sulfate-Reducing Bacterium SRB-Z Isolated from Pearl River on the Corrosion Behavior of Q235 Carbon Steel

Corrosion Behaviors of Q235 Steel in Seawater Containing Sulfate-Reducing Bacteria

Mechanism of Microbiologically Influenced Corrosion of X65 Steel in Seawater Containing Sulfate-Reducing Bacteria and Iron-Oxidizing Bacteria

Characteristics of Themicrobiologically Influenced Corrosion of 304 Stainless Steel in Reclaimed Water Enviroment

Influence of Sulfate-Reducing Bacteria on Corrosion Behavior of EQ70 High-Strength Steel

Pitting Corrosion Behavior of 316l Stainless Steel in the Media of Sulphate-Reducing and Iron-Oxidizing Bacteria

Effect of pH regulation by sulfate-reducing bacteria on corrosion behaviour of duplex stainless steel 2205 in acidic artificial seawater

The Corrosion of Two Aluminium Sacrificial Anode Alloys in SRB-containing Sea Mud

Corrosion of Antibacterial Cu-bearing 316L Stainless Steels in the Presence of Sulfate Reducing Bacteria