Solid State Reaction Preparation and Enhanced Red Luminescence of S-Doped La2mo2o9:Pr3+ Phosphors

Dandan Zhang,Shikao Shi,Ming Luo,Ji Zhou

DOI: https://doi.org/10.1016/j.ceramint.2013.01.052

IF: 5.532

2013-01-01

Ceramics International

Abstract:Red-light-emitting phosphors of La2Mo2O9:Pr3+ and S-doped La2Mo2O9:Pr3+ were prepared by high temperature solid state reaction. Under the excitation of 450nm blue light, all samples produced a red emission peak at 650nm corresponding to the characteristic transition of Pr3+ (3P0→3F2). The dependence of Pr3+ doping content (x) on the luminescent intensity was analyzed, and the optimal doping content of Pr3+ was x=0.07. After a small quantity of sulfur was introduced into the system, the luminescence intensity of phosphors was obviously enhanced. The reasons for the enhancement of luminescence are due to improved crystallization after S doping and the relatively large electronegativity difference between S and Mo. Additionally, the coincidence of the excitation wavelength with the emission of GaN chips may recommend this phosphor system as a potential candidate for use in white light-emitting diodes.