Study on processing properties of halogen-free flame-retardant LLDPE/LDPE/POE with silane crosslinking
Yajie DAI,Tian MIAO,Wenlong ZHANG,Yuling SHAN
DOI: https://doi.org/10.3969/j.issn.1001-9731.2019.01.025
2019-01-01
Abstract:In this paper, the silane cross-linking halogen-free flame-retardant polyolefin cable material was easy to absorb water, resulting in poor cross-linking and extrusion.The silane couple was compounded with magnesium hydroxide (MH) and aluminum hydroxide (ATH) flame retardant.Silane crosslinked LLDPE/LDPE/POE halogen-free flame retardant materials were prepared by melt blending.The effects of flame retardant on the processing properties before and after silane treatment and the effects of different ratios of MH and ATH on its mechanical properties, oxygen index and thermal elongation were investigated.The results showed that the surface of the hydroxide flame retardant treated by silane coupling was smoother than that of the untreated extruded composite sheet, and the rheological property was good.There was no pre-crosslinking.At this time, the balance torque dropped by 24.8％, and the melt flow rate increased by 23.5％.With the increased of MH/ATH ratio, the oxygen index and tensile strength of the composites increased firstly and then decreased, but the thermal elongation, permanent deformation rate and elongation at break showed a trend of decreasing firstly and then increased.When the ratio of MH/ATH was 2/1, the composite had the best performance after 8dof water resistance test.The tensile strength reached to 17.5MPa, the elongation at break reached to 349％, the oxygen index reached to 34.2％, the thermal elongation reached 17％, and the permanent deformation rate reached to 3.3％.