Abstract:Among the inorganic nanofibers, silica nanofibers are of great interest due to high reactivity and availability of silicon compounds in nature. Sol–gel process is required for electrospinning of silica nanofibers, in which a metal alkoxide is hydrolyzed and the viscosity increased. In this study, silica nanofibrous yarn containing silver nanoparticles were synthesized and electrospun from a mixture of silica sol with an easy spinnable polymer (PVA) as an additive. The silica sol contains tetraethyl orthosilicate (TEOS), silver nitrate, distilled water, nitric acid and ethanol. Nanofiber yarn was formed through two opposite nozzle methods with the same voltage and diverse polarization. The nanofiber yarn was calcinated to remove the solvent and additive polymer. Consequently, pure silica nanofibrous yarn was produced. FTIR analysis showed entire removal of polyvinyl alcohol from the yarn structure and formation of silan groups. The presence of silver, silica and oxygen was confirmed by EDX and XRD patterns also revealed the presence of silver nanoparticles with a mean crystal size of 18 nm. FESEM images of nanofiber yarn showed the fracture surface on the yarn. Adding silver nitrate into the sol–gel resulted in decrease in nanofiber diameter from 286 to 136 nm. Tensile strength results showed higher strength and modulus of elasticity for the glass nanofiber yarn produced with PVA/sol–gel = 1:4 at 2000 turns per meter (TPM) comparing with other samples by different twist levels and sol–gel ratios. Furthermore, the electrospun glass yarn showed more resistance in acidic media than alkaline media.Preparation of silica sol contains TEOS, silver nitrate, distilled water, nitric acid and ethanol for synthesize of silica nanofibrous yarn containing silver nanoparticles through electrospun. The presence of silver nitrate into the sol–gel resulted in finer nanofiber with 136 nm.

Fabrication of silica nano/micro-fibers doped with one-dimensional assembly of silver nanoparticles.

Silica Nanofibers and Subwavelength-Diameter Fibers

Aqueous-Based Coaxial Electrospinning of Genetically Engineered Silk Elastin Core-Shell Nanofibers

Mesoporous Silica Fibers Prepared by Electroblowing of A Poly(Methyl Methacrylate)/Tetraethoxysilane Mixture in N,N-Dimethylformamide

Fabrication of silica nanoparticles with both efficient fluorescence and strong magnetization, and exploration of their biological applications

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Thermoplastic polyurethane/silica nanocomposite fibers by electrospinning

Glass nanofibrous yarn through electrospinning along with in situ synthesis of silver nanoparticles

Poly(Methyl Methacrylate)/Silica Nanocomposite Fibers by Electrospinning

Sol-gel Preparation of Ag-silica Nanocomposite with High Electrical Conductivity

Fabrication of One-Dimensional Iron Oxide/Silica Nanostructures with High Magnetic Sensitivity by Dipole-Directed Self-Assembly

Fabricating Highly Ordered Nanofiber Assemblies by Controlled Shear Flow and Solvent Evaporation

Formation of Gold and Silver Nanoparticle Arrays and Thin Shells on Mesostructured Silica Nanofibers

Centrifugal Spinning Enables the Formation of Silver Microfibers with Nanostructures

Fabrication of silver/silver-tetracyanoquinodimethane heterogeneous nanowires using nanoskiving method

Composite Silicon Nanostructure Arrays Fabricated on Optical Fibre by Chemical Etching of Multicrystal Silicon Film.

Fabrication of Mesoporous Dendritic Silica Nanofibers by Using Dendritic Polyaniline Templates

Fabrication of a 3D Porous Silver Wire Based on a Template-Assisted Electroless Deposition Method

Fabricating Nanostructure Materials by Electrospinning Technique

Microstructural Ordering of Nanofibers in Flow-Directed Assembly

Nanostructured LiCoO2 and LiMn2O4 fibers fabricated by a high frequency electrospinning