Abstract:Quaternary chalcogenide Cu 2 CoSnS 4 (CCTS) thin films were successfully prepared by spray pyrolysis on glass substrates in varying the precursor concentration and the thiourea volume. The effects of the precursor concentration and the thiourea volume on the formation of the CCTS phase were systematically investigated by X-ray diffraction, Raman spectroscopy, Energy-Dispersive X-ray Spectroscopy. The electrical resistivity at room temperature has been measured by the four probes method. It is shown that the crystallization of the stannite CCTS phase depends on both the precursor concentration and thiourea volume. The minimum volume of thiourea required to crystallize the CCTS phase depends on the precursor concentration, i.e. the CCTS crystallization needs higher volume of thiourea at low precursor concentration. For higher precursor concentration, the CCTS is poorly crystallized with the presence of secondary phases such as CuS 2 , CoS 2 , and CuCo 2 S 4 , while the crystallization domain is relatively large. The CCTS well crystallizes only in a narrow range of precursor concentration and thiourea volume. The relatively poor crystallization combined with the presence of secondary phases are harmful for the optical and electrical features of the CCTS film. Besides, optical transmission measurements of the optimized film showed an optical gap of 1.7 eV (~ 730 nm) and an absorption coefficient included between 10 4 and 10 5 cm −1 in the visible solar range. Furthermore, the optimized stannite CCTS films are compact exhibiting a relatively rough and granular surface due to the formation of copper sulfide nodules. The electrical resistivity of the optimized CCTS film is about 0.4 10 –2 Ω cm. These results suggest that the deposited films fit the requirements of absorbing layer in solar cells. The diode composed of Au/Cu 2 CoSnS 4 /SnO 2 films was investigated with current–voltage ( I – V ) measurements performed under dark and bright conditions. The series resistance, saturation current and ideality factor of typical diode is estimated to be 689 Ω, 1.15 10 –5 A and 3, respectively.

Colloidal Synthesis of Wurtzite Cu2CoSnS4 Nanocrystals and the Photoresponse of Spray-Deposited Thin Films

Colloidal Synthesis of Wurtzite Cu2fesns4 Nanocrystals

Colloidal Synthesis of Quaternary Wurtzite Cu3 AlSnS5 Nanocrystals and Their Photoresponsive Properties.

Facile Synthesis of Ultra-Long Cu2CdSnS4 Nanowires with Wurtzite-Derived Structure

Colloidal Nanocrystals of Wurtzite-Type Cu2znsns4: Facile Noninjection Synthesis and Formation Mechanism

Colloidal Synthesis and Optical Properties of Metastable Wurtzite I3-III-IV-VI5 (cu3insns5) Nanocrystals

Facile One-Pot Synthesis and Optical Properties of Quinary Wurtzite Cu3zninsns6 Nanocrystals

A Facile Arrested Precipitation Method for Synthesis of Pure Wurtzite Cu2ZnSnS4 Nanocrystals Using Thiourea As a Sulfur Source

Colloidal Synthesis of Wurtzite CuInS2 Nanocrystals and Their Photovoltaic Application

Crystal phase-controlled synthesis of Cu 2FeSnS 4 nanocrystals with a band gap of around 1.5 eV

Insight into the Crystal Phase and Shape Evolution from Monoclinic Cu1.94S to Wurtzite Cu2ZnSnS4 Nanocrystals

Synthesis and Characterization of Cu2CoSnS4 Thin Films Prepared Via Radio-Frequency (RF) Magnetron Sputtering

Controlled Synthesis of Wurtzite CuInS2 Nanocrystals and Their Side-by-side Nanorod Assemblies

Phase-selective and Photoactivity Investigation of Solvothermal Synthesized Cu2ZnSnS4 Nanoparticles

Facile hydrothermal synthesis of hydrotropic Cu2ZnSnS 4 nanocrystal quantum dots: Band-gap engineering and phonon confinement effect

Colloidal Nanocrystals of Orthorhombic Cu2znges4: Phase-Controlled Synthesis, Formation Mechanism and Photocatalytic Behavior

Synthesis and Characterization of Colloidal CZTS Nanocrystals by a Hot-Injection Method

Synthesis, Growth and Characterization of Cu2CoSnS4 Thin Films via Thermal Evaporation Method

Wurtzite Cu 2ZnSnS 4 nanocrystals: A novel quaternary semiconductor

Synthesis of Shape-Controlled Monodisperse Wurtzite CuInxGa1–xS2 Semiconductor Nanocrystals with Tunable Band Gap

Synthesis of Cu2CoSnS4 chalcogenide thin films by spray pyrolysis and efficient Au/p-CCTS/n-SnO2 diode for cells solar applications