Size-controlled synthesis and photoluminescence of porous monolithic α-alumina

Shifa Wang,Xia Xiang,Qingping Ding,Xiaolin Gao,ChunMin Liu,Zhijie Li,Xiaotao Zu

DOI: https://doi.org/10.1016/j.ceramint.2012.09.068

IF: 5.532

2013-01-01

Ceramics International

Abstract:A modified polyacrylamide gel route is used to synthesize porous monolithic α-alumina. X-ray powder diffraction analysis indicates that the as-prepared samples are rhombohedral α-alumina phase, suggesting that high-purity α-alumina can be prepared by using different chelating agents and sintering at about 1150°C. The scanning electron microscopic images show that the macropore size of the α-alumina samples is related to the chelating agent. The photoluminescence spectra show that a major emission band around 365nm and a weaker side band located at 330nm are observed when the excitation wavelength is 228nm. Interestingly, the intensity of emission peak at 365nm decreases with the decreasing pore size. The pore-forming and luminescence mechanisms of porous alumina have been discussed based on the experimental results.