Abstract:The La2Ce2O7 (LC) coating with the La/Ce ratio close to 1 was obtained by atmospheric plasma spraying, using La2Ce2.5O8 as a feedstock powder and optimized spray parameters. The spray distance plays a significant role in terms of phase composition, phase stability, as well as porosity of the LC coating, while keeping other spray parameters constant. The plasma-sprayed coatings were prepared and thermally cycled by gas-burner tests to evaluate thermal cycling lifetime. The thermal cycling lifetime of the LC/YSZ double-layer coating was more than three times the lifetime of a single-layer LC coating and comparable to the YSZ coating at operating temperature of ∼1230°C. The thermal cycling lifetimes of the LC/YSZ coating were ∼40% longer at operating temperature of ∼1320°C, but much lower at operating temperature of ∼1350°C compared to the optimized YSZ coating. The failure mechanisms for the LC and LC/YSZ coatings thermally cycled under different conditions were also established in this work.

Optimization and Thermal Cycling Behavior of La2ce2o7 Thermal Barrier Coatings