Biosynthesized Bimetallic Au–Pd Nanoparticles Supported on TiO2 for Solvent-Free Oxidation of Benzyl Alcohol
Yingling Hong,Xiaolian Jing,Jiale Huang,Daohua Sun,Tareque Odoom-Wubah,Feng Yang,Mingming Du,Qingbiao Li
DOI: https://doi.org/10.1021/sc500181z
IF: 8.4
2014-01-01
ACS Sustainable Chemistry & Engineering
Abstract:A green bioreductive approach with Cacumen Platycladi (CP) extract was adopted to fabricate bimetallic Au-Pd/TiO2 catalysts for solvent-free oxidation of benzyl alcohol (BzOH) to benzaldehyde (BzH) with molar oxygen at atmospheric pressure. The Au-Pd nanoparticles (NPs) before being immobilized onto TiO2 were determined by transmission electron microscopy. And, the catalysts were further analyzed by X-ray diffraction, X-ray photoelectron spectroscopy, thermogravimetric analysis, etc. Effects of Au/Pd molar ratio, preparation conditions, and reaction conditions on the catalytic activity of Au-Pd/TiO2 were investigated. And, the Au-Pd/TiO2 catalyst without calcination that was prepared at 90 degrees C from the Au-Pd NPs with Au/Pd molar ratio of 2:1 exhibited excellent catalytic performance. With the catalyst, BzOH conversion of 74.2% and selectivity to BzH 95.8% were attained at the reaction temperature of 90 degrees C with an oxygen flow rate of 90 mL/min. Meanwhile, the recycling tests showed that, after seven recycles, the catalyst still remained with high conversion and selectivity. Therefore, the catalyst had excellent durability and reusability and good prospects for industrial application.