Intercalated rare earth hydrotalcite‐like materials and their application in stabilizers in poly (vinyl chloride)
Guifang Du,Zhaogang Liu,Peijie Jia,Jinsheng Duan,Ruifeng Ma,Yonggang Liu,Fushan Feng,Yanhong Hu,Jinxiu Wu
DOI: https://doi.org/10.1002/vnl.21983
2023-03-02
Journal of Vinyl and Additive Technology
Abstract:The mechanism of action of hydrotalcite‐like heat stabilizers is to absorb the HCl released during the thermal degradation of PVC and produce metal chloride. The intercalated itaconic acid roots lie in the reaction with the CC conjugated double bonds produced by the thermal degradation of PVC. It is that can be achieved by reducing the production of CC double bonds during the thermal degradation of PVC and inhibiting the production of HCl. In this research, ZnAlLa‐itaconate‐LDHs was synthesized by means of Co‐precipitation‐hydrothermal method. The effects of aluminum‐lanthanum ratio, co‐precipitation time, hydrothermal time, and hydrothermal temperature on the crystal structure were studied. As a result, the optimum condition was found to be: n(Al3+): n(La3+) = 10:1, co‐precipitation time 24 h, hydrothermal time 8 h, and hydrothermal temperature 180°C. The influence of ZnAlLa‐itaconate‐LDHs on the thermal stability properties and plasticizing properties of PVC were investigated, exhibiting long‐term stability of 76 min with short plasticizing time of 1.11 min. Long‐term thermal stability mechanism was studied by FTIR before and after hydrochloric acid treatment. It was demonstrated that the thermal stabilizer ZnAlLa‐itaconate‐LDHs prevented the rupture of the CCl bond in PVC and inhibited the development of HCl. Consequently, impeded the production of CC bond and playing a role in thermal stabilization of PVC.
chemistry, applied,materials science, textiles,polymer science