Synthesis and Characterization of Stable Cu-Pt Nanoparticles under Reductive and Oxidative Conditions
Alexandre C Foucher,Shengsong Yang,Daniel J Rosen,Renjing Huang,Jun Beom Pyo,Ohhun Kwon,Cameron J Owen,Dario Ferreira Sanchez,Ilia I Sadykov,Daniel Grolimund,Boris Kozinsky,Anatoly I Frenkel,Raymond J Gorte,Christopher B Murray,Eric A Stach
DOI: https://doi.org/10.1021/jacs.2c13666
2023-03-08
Abstract:We report a synthesis method for highly monodisperse Cu-Pt alloy nanoparticles. Small and large Cu-Pt particles with a Cu/Pt ratio of 1:1 can be obtained through colloidal synthesis at 300 °C. The fresh particles have a Pt-rich surface and a Cu-rich core and can be converted into an intermetallic phase after annealing at 800 °C under H2. First, we demonstrated the stability of fresh particles under redox conditions at 400 °C, as the Pt-rich surface prevents substantial oxidation of Cu. Then, a combination of in situ scanning transmission electron microscopy, in situ X-ray absorption spectroscopy, and CO oxidation measurements of the intermetallic CuPt phase before and after redox treatments at 800 °C showed promising activity and stability for CO oxidation. Full oxidation of Cu was prevented after exposure to O2 at 800 °C. The activity and structure of the particles were only slightly changed after exposure to O2 at 800 °C and were recovered after re-reduction at 800 °C. Additionally, the intermetallic CuPt phase showed enhanced catalytic properties compared to the fresh particles with a Pt-rich surface or pure Pt particles of the same size. Thus, the incorporation of Pt with Cu does not lead to a rapid deactivation and degradation of the material, as seen with other bimetallic systems. This work provides a synthesis route to control the design of Cu-Pt nanostructures and underlines the promising properties of these alloys (intermetallic and non-intermetallic) for heterogeneous catalysis.