Abstract:Degradable thermosensitive ionic microgels were synthesized via surfactant-free emulsion polymerization.(SEEP), N-isopropylacrylamide (NIPAm) and 1-vinylimidazole :(VIM) at 70 degrees C with degradable 1,4-phenylene bis(4-bromobutanoate) or 1,6-hexanediol bis(2-bromopropionate) as quaternized cross-linkers. VIM could be,quaternized by 1,4-phenylene bis(4-bromobutanoate) or 1,6-hexanediol bis(2-bromopropionate), leading to the formation of degradable cross-linking network and ionic microgels. Combined techniques of transmission electron microscopy (TEM), dynamic light scattering (DLS), electrophoretic light scattering (ELS), UV-vis spectroscopy, FT-IR spectra, and gel permeation chromatography (GPC) were employed to systematically investigate the sizes, morphologies, and properties of the obtained microgels before and after degradation as well as the degradation mechanism. The obtained microgels were spherical in shape with narrow size distribution and exhibited thermosensitive behavior and controllable degradation. The disintegration of the microgels was confirmed to be resulted from the hydrolysis of ester bonds of the cross-linkers. The degradation rate of the obtained microgels could be regulated by tuning the pH value of niicrogel suspensions. The PNI-Ph series of microgels fabricated with 1,4-phenylene bis(4-bromobutanoate) as the cross-linking agent could gradually degrade even in neutral solution with lifetime S' of 44-53 h, depending On the quaternizaiton ratio. The degradation of PNI-Ph series of microgels experienced two reaction processes, that is, the hydrolysis of ester bonds of the cross-linkers and the oxidation of generated hydroquinone to form benzoquinone. It was also demonstrated that different silica nanostructures could be fabricated by Using such degradable thermosensitive ionic microgels as the template at various temperatures.

In Situ Generation of Bioreducible and Acid Labile Nanogels/microgels Simply Via Adding Water into the Polymerization System

Bioreducible Nanogels/microgels Easily Prepared Via Temperature Induced Self-Assembly and Self-Crosslinking

Degradable and Thermosensitive Microgels Synthesized Via Simultaneous Quaternization and Siloxane Condensation

Formation of Microgels by Utilizing the Reactivity of Catechols with Radicals

Facile synthesis of size‐tunable multihydroxy nanogels by self‐assembly‐induced disulfide bonds crosslinking

Tuning the Morphology, Network Structure, and Degradation of Thermo-Sensitive Microgels by Controlled Addition of Degradable Cross-Linker

Thermosensitive Ionic Microgels with Ph Tunable Degradation Via in Situ Quaternization Cross-Linking

Degradable and Thermosensitive Microgels with Tannic Acid As the Sole Cross-Linker

Multiresponsive Microgels with Phase-Separated Nanodomains and Self-Regulating Properties Via Incorporation of Anthraquinone Moieties.

Thermosensitive ionic microgels via surfactant-free emulsion copolymerization and in situ quaternization cross-linking.

In Situ Synthesis of Poly(Acrylic Acid) Physical Hydrogels from Silica Nanoparticles

In situ rapid synthesis of hydrogels based on a redox initiator and persistent free radicals

Tough, Stretchable, Compressive Double Network Hydrogel Using Natural Glycyrrhizic Acid Tailored Low-Molecular-Weight Gelator Strategy: in Situ Spontaneous Formation of Au Nanoparticles to Generate a Continuous Flow Reactor.

Responsive nanotubular organo-gelator

Au–polymer Hybrid Microgels Easily Prepared by Thermo-Induced Self-Crosslinking and in Situ Reduction

One-Pot Synthesis of Oxidation-Sensitive Supramolecular Gels and Vesicles

Two Approaches for the Engineering of Homogeneous Small-Molecule Hydrogels

In-situ swelling of pH-responsive microgel particles during photopolymerization to mitigate shrinkage stress of UV-cured materials

Self‐immolative Polymer Hydrogels via In Situ Gelation

Successive Redox-Reaction-Triggered Interface Radical Polymerization for Growing Hydrogel Coatings on Diverse Substrates.

Stretchable Sponge-like Hydrogels with a Unique Colloidal Network Produced by Polymerization-Induced Microphase Separation