Abstract:A silica gel supported CuBr-hexamethyltriethylenetetramine (HMTETA) (SG-CuBr/HMTETA) catalyst system was developed for the synthesis of poly-(methyl methacrylate) (PMMA) and poly(dimethylaminoethyl methacrylate) (polyDMAEMA) macromonomers with terminal vinyl or allyl group by atom transfer radical polymerization (ATRP). Catalyzed by SG-CuBr/HMTETA and with vinyloxyethyl 2-bromoisobutyrate (VBIB) or allyl 2-bromoisobutyrate (ABIB) as initiator, the MMA polymerization showed first order kinetics up to a 60% monomer conversion. The polymerization rate slowed down at higher conversions due to a reduction in radical concentration. Gel permeation chromatography (GPC) results showed that the decrease in radical concentration was caused by the reaction of radicals with the initiator's vinyl or allyl group moieties. In contrast, the DMAEMA polymerization was first order kinetics throughout the polymerization. The molecular weights of the resulting PMMA and polyDMAEMA increased linearly with conversion with low polydispersities. After the first run polymerization, the catalysts were recycled for second and third runs. The recycled catalysts still mediated a living polymerization of MMA or DMAEMA, producing polymers with controlled molecular weight and narrow polydispersity, but their catalytic activities decreased significantly. The reactivity reduction of the recycled catalyst was due to radical side reactions that yielded an extra amount of CuBr2 as well as the catalyst loss during recycling.

Facile synthesis of gradient copolymers via semi-batch copper(0)-mediated living radical copolymerization at ambient temperature

Model-based design and synthesis of gradient MMA/tBMA copolymers by computer-programmed semibatch atom transfer radical copolymerization

Synthesis of Polymer Thin Film Gradient with Nanometer Thickness through Water Diffusion Controlled Surface Polymerization

Semibatch RAFT Polymerization for Producing ST/BA Copolymers with Controlled Gradient Composition Profiles

Well-controlled and stable emulsion ATRP of MMA with low surfactant concentration using surfactant–ligand design as the copper capture agent

Gradient copolymers of epsilon-caprolactone and delta-valerolactone via solvent-free ring-opening copolymerization with a pyridyl-urea/MTBD system

Control of Gradient Copolymer Composition in Atrp Using Semibatch Feeding Policy

Programmed Synthesis Of Copolymer With Controlled Chain Composition Distribution Via Semibatch Raft Copolymerization

Tailor-made compositional gradient copolymer by a many-shot RAFT emulsion polymerization method

Controlled Polymerization of Methyl Methacrylate and Styrene Via Cu(0)-Mediated RDRP by Selecting the Optimal Reaction Conditions

Dispersion Atom Transfer Radical Polymerization of Vinyl Monomers in Supercritical Carbon Dioxide

Controlled Polymerization of Acrylamide via One-Pot and One-Step Aqueous Cu(0)-Mediated Reversible-Deactivation Radical Polymerization

Synthesis of gradient copolymers by concurrent enzymatic monomer transformation and RAFT polymerization

Copper-Mediated CRP of Methyl Acrylate in the Presence of Metallic Copper: Effect of Ligand Structure on Reaction Kinetics

Living Radical Polymerization Of Methyl Methacrylate Catalyzed By Cuprous N,N-Diethyldithiocarbamate

Facile synthesis of gradient copolymers enabled by droplet-flow photo-controlled reversible deactivation radical polymerization

Atom Transfer Radical Polymerization of Methyl Methacrylate by Silica Gel Supported Copper Bromide/Multidentate Amine

"Living" Radical Polymerization of Methyl Methacrylate Using CuBr as Catalyst in [Hmim][CH_3COO]

Continuous Atom Transfer Radical Block Copolymerization of Methacrylates

Soluble and Recoverable Support for Copper Bromide-Mediated Living Radical Polymerization

Synthesis of Methacrylate Macromonomers Using Silica Gel Supported Atom Transfer Radical Polymerization