Abstract:Although widely used as proton-exchange membranes (PEMs), perfluorosulfonic acid (PFSA) membranes suffer from critical mechanical degradation under alternating wet/dry conditions. A common method for improving the mechanical durability of PFSA mem-branes is to intercalate single-layer expanded polytetrafluoroethylene (ePTFE). As rein-forcement skeletons, the different numbers of ePTFE layers can be expected to have different effects on the mechanical durability of PFSA-based PEMs. In this study, double layers of ePTFE reinforcement are intercalated into PFSA ionomer to further enhance the mechanical durability of such membranes. The mechanical strength in directions A and B of the double-layer ePTFE reinforced membrane (DR-M) are 36.52 and 37.12 MPa, which are significantly higher than those (24.37 and 27.51 MPa) of the single-layer ePTFE reinforced membrane (SR-M). The area swelling rate of the DR-M is 11.91%, which is lower than that (15.53%) of SR-M. It is precisely due to the additional rigid ePTFE skeleton for the DR-M that the yield strength and modulus of the PFSA membrane are further improved, resulting in the higher resistance to plastic deformation. After 3000 cycles of alternating wet/dry conditions, DR-Ms exhibited no significant hydrogen crossover current increase (from 3.01 mA cm-2 to 2.98 mA cm-2), reduced H2/Air fuel cell performance attenuation (by 4.9%), smaller membrane impedance increase (by 6.2%), and reduced membrane structure failure (less cracks) compared with SR-Ms. In short, the described double-layer ePTFE enhance-ment strategy provided a fresh perspective for improving the mechanical durability of PEMs.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Enhanced Chemical Durability of Perfluorosulfonic Acid Membranes Through Incorporation of Terephthalic Acid As Radical Scavenger

Enhanced stability of PFSA membranes for fuel cells: Combined effect between supercritical carbon dioxide treatment and radical scavenger incorporation

A Kinetic Model for the Chemical Degradation of Perfluorinated Sulfonic Acid Ionomers: Weak End Groups Versus Side Chain Cleavage

Durability Improvement for Eptfe Reinforced Perfluorosulfonic Acid Membranes by Natural Organic Free Radical Scavengers

Aspects of the Chemical Degradation of Pfsa Ionomers Used in Pem Fuel Cells

Ce (III)-terephthalic acid metal-organic frameworks as highly efficient ·OH radical scavengers for fuel cells and investigation of its antioxidation mechanism

Mitigation of chemical degradation in perfluorosulfonic acid proton exchange membrane using regenerable hindered amine functionalized carbon quantum dots

Expanded polytetrafluoroethylene functionalized with free radical scavengers and hydrophilic groups for superior chemical stability of proton exchange membranes

Grafting free radical scavengers onto polyarylethersulfone backbones for superior chemical stability of high temperature polymer membrane electrolytes

Enhanced mechanical durability of perfluorosulfonic acid proton-exchange membrane based on a double-layer ePTFE reinforcement strategy

Durability enhancement of proton exchange membrane fuel cells by ferrocyanide or ferricyanide additives

Durable Perfluorosulfonic Polymer Electrolyte Membranes Prepared from Alkaline-Ion-Assisted Heat Treatment

Evaluating the Durability of Perfluorosulfonic Acid Membranes in Fuel Cells Using Combined Open-Circuit Voltage-Accelerated Stability Testing

Reinforced Composite Membranes Based on Expanded Polytetrafluoroethylene Skeletons Modified by a Surface Sol–Gel Process for Fuel Cell Applications

A composite proton exchange membrane with three-dimensionally-reinforced hydrogen bonding network for durable hydrogen fuel cells

Enhanced Mitigation of Membrane Fouling and Degradation of Perfluorooctanoic Acid in the Treatment of Natural Surface Water Through the Application of Dielectric Barrier Discharge/sulfite

Facile Preparation of Triazole-Functionalized Poly(arylene Perfluorophenyl) High Temperature Proton Exchange Membranes Via Para-Fluoro-thiol Click Reaction with High Radical Resistance

Immobilized hindered amine radical scavenger for durability enhancement of perfluorosulfonic acid membrane in PEMFCs

Chemical stability of proton exchange membranes synergistically promoted by organic antioxidant and inorganic radical scavengers

Double-Layer Expanded Polytetrafluoroethylene Reinforced Membranes with Cerium Oxide Radical Scavengers for Highly Stable Proton Exchange Membrane Fuel Cells

Durability improvement of proton exchange membrane fuel cells by doping silica‒ferrocyanide antioxidant