Abstract:The Pt/Au Schottky contacts to InGaN samples with different background carrier concentrations are fabricated. The crystal qualities of InGaN samples are characterized by X-ray diffraction (XRD) and atomic force microscope (AFM), and the correlation between threading dislocation density of InGaN and growth temperature is further clarified. The full width at half maximum (FWHM) values of the InGaN (0002) XRD rocking curves show that the density of threading dislocations in InGaN, which can seriously deteriorate InGaN crystal quality and surface morphology, decreases rapidly with increasing growth temperature. The Hall measurements show that the background carrier concentration of InGaN increases by two orders of magnitude as growth temperature decreases from 750 to 700℃, which is due to a reduced ammonia decomposition efficiency leading to the presence of high-density donor-type nitrogen vacancy (VN) defects at lower temperature. Therefore, combining the studies of XRD, AFM and Hall, it can be concluded that the higher growth temperature is favorable for realizing the InGaN film with low density of VN defects and threading dislocations for fabricating high-quality Schottky contacts, and then the barrier characteristics and current transport mechanism of Pt/Au/n-InGaN Schottky contact are investigated by current-voltage measurements and theory analysis based on the thermionic emission (TE) model and thermionic field emission (TFE) model. The results show that Schottky characteristics for InGaN with different carrier concentrations manifest obvious differences. It is noted that the high carrier concentration leads to the Schottky barrier height and the ideality factor obtained by TE model are quite different from that by TFE model due to the presence of high density of VN defects. This discrepancy suggests that the VN defects lead to the formation of the tunneling current and further reduced Schottky barrier height. Consequently, the presence of tunneling current results in the increasing of total transport current, which means that the defects-assisted tunneling transport and TE constitute the current transport mechanism in the Schottky. However, the fitted results obtained by TE and TFE models are almost identical for the InGaN with lower carrier concentration, indicating that TE is the dominant current transport mechanism. The above studies prove that the Pt/Au/n-InGaN Schottky contact fabricated using low background carrier concentration shows better Schottky characteristics. Thus, the properly designed growth parameters can effectively suppress defects-assisted tunneling transport, which is crucial to fabricating high-quality Schottky devices.

Forward Current Transport Mechanism and Schottky Barrier Characteristics of a Ni/Au Contact on N-Gan

Forward Current Transport Mechanisms of Ni/Au—InAlN/AlN/GaN Schottky Diodes

Current Transport Mechanism of Schottky Contact of Pt/Au/n-InGaN

Study of the Leakage Current Mechanism in Schottky Contacts to Al0.25Ga0.75N/GaN Heterostructures with AlN Interlayers

Performance Comparison of Pt/Au and Ni/Au Schottky Contacts on Alxga1-X N/Gan Heterostructures at High Temperatures

Current Transport Mechanisms in Pt/Au Schottky Contacts to AlInGaN Using AlGaN/InGaN Short-Period Superlattices

Thermal annealing behaviour of Al/Ni/Au multilayer on n-GaN Schottky contacts

Current-Voltage Characteristic of Alloyed Ni/Au on p-GaN

Temperature Dependence of the Specific Resistance in Ti/Al/Ni/Au Ohmic Contacts on (nh4)2sx Treated N-Type GaN

Schottky Barrier Height Inhomogeneity of Ti/n-GaAs Contact Studied by the I-V-T Technique

High-Quality Schottky Contacts to N-Ingan Alloys Prepared for Photovoltaic Devices

A study of current‐voltage and capacitance‐voltage characteristics of Au/n‐GaAs and Au/GaN/n‐GaAs Schottky diodes in wide temperature range

Current transport in Ni Schottky barrier on GaN epilayer grown on free standing substrates

Schottky Barrier Height Inhomogeneities of Nickel Mono-Silicide/N-Si Contact Studied by I-V-T Technique

Reverse Leakage Mechanism of Schottky Barrier Diode Fabricated on Homoepitaxial Gan

Current Transport Mechanism of Au∕Ni∕GaN Schottky Diodes at High Temperatures

Comparative Study on Schottky Contact Behaviors between Ga- and N-Polar GaN with SiNx Interlayer

Temperature dependent electron transport and interface state studies on Ni/n-Si/Al/Ag lateral Schottky junction

Forward Tunneling Current in Gan-Based Blue Light-Emitting Diodes

Ohmic Contact Mechanism of Ni/Au Contact to P-Type Gan Studied by Rutherford Backscattering Spectrometry

Schottky Barrier and Contact Resistance of InSb Nanowire Field Effect Transistors