Visible-Light-Induced Reversible Photochemical Crystal–Liquid Transitions of Azo-Switches for Smart and Robust Adhesives
Xianhui Huang,Zhichun Shangguan,Zhao-Yang Zhang,Chunyang Yu,Yixin He,Dong Fang,Wenjin Sun,Yan-Chun Li,Chenrui Yuan,Si Wu,Tao Li
DOI: https://doi.org/10.1021/acs.chemmater.1c03881
IF: 10.508
2022-03-08
Chemistry of Materials
Abstract:Photochemical crystal ↔ liquid transitions (PCLTs) are interesting phenomena that couple reversible photochemical transformations with thermophysical phase transitions. A potential application of PCLTs is the development of photoresponsive smart materials capable of exerting reversible adhesion capacities on specific surfaces at a desired timing, which are unattainable for conventional adhesives. However, PCLT-based adhesives generally use UV light as the stimulus, which could lead to degradation of materials and health problems. Here, visible-light-controlled smart and robust adhesives are developed using small-molecule azo photoswitches. These azo molecules can undergo very efficient trans-crystal → cis-liquid and cis-liquid → trans-crystal transitions under 405 and 532 nm light irradiations, respectively. Their trans-crystal state displays strong adhesion strengths on various substrates, e.g., 1.13 MPa on quartz/quartz and 1.58 MPa on wood/wood, and very fast light-induced separation of glued substrates can be accomplished within 1 s along with the loss of adhesion strength in the cis-liquid state. Robust switching of the adhesion strength is demonstrated in multiple cycles, and these adhesives can also work well in underwater environments. Visible-light-controlled reversible PCLTs can be a very promising strategy in the pursuit of high-performance photoresponsive adhesives.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c03881.Synthesis and characterization of M1, M2, and M3, their visible-light-controlled photochemical crystal–liquid transition behaviors, adhesion strength measurements, and theoretical calculations (PDF)Crystallographic data of M2 (CIF)Visible-light-controlled photochemical crystal ↔ liquid transition behaviors of M1 (AVI)Visible-light-controlled photochemical crystal ↔ liquid transition behaviors of M2 (AVI)Visible-light-controlled photochemical crystal ↔ liquid transition behaviors of M3 (AVI)Trans-M2-glued quartz plates lifting a weight of 18.5 kg (AVI)Separation of two bonded quartz plates under 405 nm light irradiation (50 mW cm–2) (no weight and the separation of two quartz plates achieved in 28.8 s) (AVI)Separation of two bonded quartz plates under 405 nm light irradiation (AVI)Stability test of adhesive M2 by knocking and dropping on the desk (AVI)Joint immersion in water for 30 days (AVI)Joint holding a weight of 200 g for more than 3 days in water (AVI)Separation of two bonded quartz plates under 405 nm light irradiation in water (AVI)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical