Influences of Zr on Carbide and Property of Cast M951 Alloy

ZHOU Peng-jie,HE Xiang-ming

DOI: https://doi.org/10.3969/j.issn.1001-4977.2012.10.016

2012-01-01

Abstract:Optical microscope, scanning electron microscope, electron probe micro analysis and X-ray diffraction were employed to researching the influence of Zr on the primary carbide and properly of cast superalloy. The results show that the additions Zr change the morphology and distribution of MC carbide remarkably. With the increasing Zr content, the intragranular carbide decreases, while the carbide around the grain boundary increases. And the morphologies of carbide transfer from platelet-like and needle-like to discontinuous blocky-like. EDS analysis shows that the carbide in platelet-like contains low Zr element, the dominant composition is Nb and C, while nearly half of Nb is substituted by Zr in blocky carbide. The lattice parameter of MC carbide rises if doped with Zr. The creep rupture life of the alloy at 1100°C/40 MPa increases with increasing Zr content first, then decreases, the peak life is 77.8 h when Zr concentration reaches 0.049%. The tensile strength rises slowly with the increment of Zr, and the elongation also improves.