Fracture mechanism of tungsten fiber reinforced ZrTiCuNiBeNb metallic glass composites

王美玲,杨斌

DOI: https://doi.org/10.13289/j.issn.1009-6264.2012.10.005

2012-01-01

Abstract:Fracture mechanism of W fiber/ZrTiCuNiBeNb metallic glass composites was studied. The results show that with the W fiber volume fraction increasing, the fracture mode of composite changes from the "self-sharpening" controlled by the glass matrix to the "fiber tearing". Under compression load,the W fibers are subjected to complex stresses including bending stress and stress concentration formed due to pile-up of shear bands in martrix acting on W fibers besides the applied stresses. When the stresses are lower than fracture strength of W fiber, the matrix deformation can cut over the fibers and the composite shows "self-sharpening" characteristic. On the contrary, when stresses are higher than fracture strength of W fiber, fibers are unstable and split along the grain boundaries, the composite shows "fiber tearing" characteristics.