Abstract:In this work an intercalation-chemistry-based method to synthesize tungstate and tungsten oxide nanosheets was described. A layered bismuth tungstate (Bi2W2O9) was used as the W-containing starting material. After the bismuth oxide layers were leached by a chloride acid, a protonated form, H2W2O7 center dot xH(2)O with sizes of 5-15 mu m, was achieved. The intercalation reaction of n-octylamine with H2W2O7 center dot xH(2)O in heptane and the subsequent dissolution-recrystallization process led to the formation of tungstate-based inorganic organic hybrid nanobelts. Orthorhombic WO3 center dot H2O nanosheets were obtained by removing the organic species of the as WO3 center dot H2O nanosheets at 250-450 degrees C, monoclinic WO3 nanosheets were achieved. The results of XRD, TEM and SEM indicate that the obtained WO3 center dot H2O and WO, were single-crystalline nanosheets with areas of (200-500) nm x (200-500) nor and thicknesses of 10-30 nm. The SAED patterns suggest that the WO3 center dot H2O and WO3 nanosheets possessed a reduced directions of [010] and [001], respectively. N-2 adsorption measurement results indicate that the specific surface areas of the as-obtained WO3 center dot H2O and WO3 nanosheets were up to 250 and 180 m(2)/g, respectively. The formation mechanisms for hybrid nanobelts, WO3 center dot H2O and WO3 nanosheets were discussed. The proposed novel route was efficient in producing two-dimensional WO3 nanosheets on a large scale.

Porous tungsten carbide nanoplates derived from tungsten trioxide nanoplates

Ultrasmall and phase-pure W 2 C nanoparticles for efficient electrocatalytic and photoelectrochemical hydrogen evolution.

Novel Pseudo-Morphotactic Synthesis and Characterization of Tungsten Nitride Nanoplates

Size- and Shape-Controlled Conversion of Tungstate-Based Inorganic-Organic Hybrid Belts to Wo3 Nanoplates with High Specific Surface Areas

Single-Crystalline Tungsten Oxide Nanoplates

Silica-templated Synthesis of Ordered Mesoporous Tungsten Carbide/graphitic Carbon Composites with Nanocrystalline Walls and High Surface Areas Via a Temperature-Programmed Carburization Route.

Novel synthesis of hierarchical tungsten carbide micro-/nanocrystals from a single-source precursor

Preparation and catalytic properties of tungsten oxides with different morphologies

Thickness Controllable and Mass Produced WC@C@Pt Hybrid for Efficient Hydrogen Production

Epitaxial Growth of Multimetallic Pd@PtM (M = Ni, Rh, Ru) Core-Shell Nanoplates Realized by in Situ-Produced CO from Interfacial Catalytic Reactions.

Controllable Synthesis of Hexagonal WO3 Nanoplates for Efficient Visible-Light-Driven Photocatalytic Oxygen Production.

Synergistic WO3·2H2O Nanoplates/WS2 Hybrid Catalysts for High-Efficiency Hydrogen Evolution

Porous Tungsten Carbo-Nitride Supported Pt Nanoparticles with High Conductivity for Efficient and Stable Hydrogen Evolution Reaction

Hierarchical WO 3 Flowers Comprising Porous Single-Crystalline Nanoplates Show Enhanced Lithium Storage and Photocatalysis

Synthesis, Characterization and Formation Mechanism of Single-Crystal Wo3 Nanosheets Via an Intercalation-Chemistry-Based Route

Tungsten carbide (WC) nanopowders synthesized via novel core–shell structured precursors

Ice-templated porous tungsten and tungsten carbide inspired by natural wood

Hierarchically Porous Carbons Derived from Nonporous Coordination Polymers.

High-yield Synthesis of Ultrathin and Uniform Bi₂WO₆ Square Nanoplates Benefitting from Photocatalytic Reduction of CO₂ into Renewable Hydrocarbon Fuel under Visible Light.

In situ Synthesis of Nano-WO3 Particles Attached to Sphere like Micro-WO3 Using Jagged CNTs as Template

ZIF-8-derived Carbon-Thin-layer Protected WC/W24O68 Micro-Sized Rods with Enriched Oxygen Vacancies As Efficient Pt Co-Catalysts for Methanol Oxidation and Oxygen Reduction