Microstructures Variation of Ti-26Nb-28Ta-5.5Zr Alloy during Compression at Room Temperature

Zhao Jie,Sun Wei,Wang Guohui

DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.05.003

2012-01-01

Abstract:With the aid of d-electron alloy theory calculation, a β-type biocompatible Ti-26Nb-28Ta-5.5Zr (%(mass fraction), K β~1.61) alloy with higher K β stability parameter was designed and prepared. Electronic universal testing machine compressing, microhardness testing, X-ray diffraction examination and transmission electron microscopy observations were applied to investigate the mechanical properties under compression, deformation mechanisms and deformation microstructural characteristics for the solution-treated Ti-26Nb-28Ta-5.5Zr alloy. The results showed that, the β-type Ti-26Nb-28Ta-5.5Zr alloy in solution-treated state had good plasticity and its compressive yield strength was 450 MPa. Dislocation glide was the dominant mechanism when the amount of compression deformation was 7%. Stress-induced α″ martensite transformation was the main plastic deformation mechanism which could have a strong influence on the characteristic of deformed microstructure when the amount of compression was 50%. In addition to the stress-induced α″ martensite transformation, non-uniform localized deformation was also found to occur when deformation amount was 75%.