Synthesis and luminescence properties of Yb 3+ –Er 3+ co-doped LaOCl nanostructures
Qingling Kong,Jinxian Wang,Xiangting Dong,Wensheng Yu,Guixia Liu
DOI: https://doi.org/10.1007/s10853-013-8003-4
IF: 4.5
2014-01-01
Journal of Materials Science
Abstract:LaOCl:Yb 3+ , Er 3+ nanofibers and hollow nanofibers were prepared by electrospinning combined with a double-crucible chlorination technique using NH 4 Cl as chlorinating agent. X-ray powder diffraction analysis indicated that LaOCl:Yb 3+ , Er 3+ nanostructures were tetragonal with space group P 4/ nmm . Scanning electron microscope analysis and histograms revealed that diameters of LaOCl:Yb 3+ , Er 3+ nanofibers and hollow nanofibers, respectively, were 117.87 ± 15.48 and 141.09 ± 17.10 nm under the 95 % confidence level. Up-conversion (UC) emission spectra analysis manifested that LaOCl:Yb 3+ , Er 3+ nanostructures exhibited strong green and red UC emission centering at 526, 548, and 671 nm, respectively, attributed to 2 H 11/2 → 4 I 15/2 , 4 S 3/2 → 4 I 15/2 , and 4 F 9/2 → 4 I l5/2 transitions of Er 3+ ions under the excitation of a 980-nm diode laser. It was found that the relative intensities of green and red emissions vary obviously with the addition of Yb 3+ ions, and the optimized molar ratio of Yb 3+ to Er 3+ was 10:1 in the as-prepared nanofibers. Moreover, the near-infrared characteristic emissions of LaOCl:Yb 3+ , Er 3+ nanostructures were achieved under the excitation of a 532-nm laser. CIE analysis demonstrated that color-tuned luminescence can be obtained by changing doping concentration of Yb 3+ (and/or Er 3+ ) ions and morphologies of nanomaterials, which could be applied in the fields of optical telecommunication and optoelectronic devices. The UC luminescent mechanism and the formation mechanisms of LaOCl:Yb 3+ , Er 3+ nanofibers and hollow nanofibers were also proposed.