Effect of Annealing Process on Microstructure and Properties of Roll-Casting AZ31B Mg Alloy Sheet
Jianping Li,Zhipeng Li,Daheng Mao,Biao Zhang,Shi Chen
DOI: https://doi.org/10.1016/j.proeng.2011.12.536
2012-01-01
Procedia Engineering
Abstract:The effect of annealing temperature and time on the microstructure and mechanical properties of AZ31B Mg alloy sheets were investigated. The specimens were deformed by general roll-casting and combining energy-field roll-casting (electromagnetic field and ultrasonic). The microstructure analysis showed that the re-crystallization temperature of combining energy-field Mg sheet was lower than that of general Mg sheet. It has been found that at the annealing of 250°C, no obvious re-crystallization occurred for the general Mg strip sheet, while the local re-crystallization occurred for the Mg strip sheet with combining energy-field roll-casting. However, in the condition of annealing at 300°C, the specimens of roll-casting Mg strips fully re-crystallized with the holding time of 4h, and the specimens with compound energy-field Mg strip had fine grains and uniform microstructure, and the average grain diameter were 14∼19μm, 8∼13μm for the general Mg strip sheet and combining energy-field Mg strip sheet, respectively. When the specimens were annealed at 400°C, the grains became coarse within 1h, the average grains diameters were 20∼25μm and 28∼33μm respectively for the general Mg roll-casting sheet and combining energy-field Mg roll-casting sheet when annealing at 400°C for 1h. The results of EDS showed that the precipitates amount of annealed Mg roll-casting sheets were reduced by annealing, the precipitates of general Mg roll-casting sheet with thicker size were enriched on the grain boundaries. The results of the mechanical properties indicated that the plastic deformation of roll-casting Mg sheets was improved significantly; Under the annealing condition of 300°C × 4h, the values of HBS, σb, σ0.2 and δ of combining energy-field Mg strip were improved by 4.7%, 17.2%, 34.1%, 74.6%, compared to general Mg sheet.