Abstract:In order to improve the calorific value and reducibility of the syngas produced by traditional coal gasification technology, and to solve the problem of high cost of heat source in coal gasification, this paper proposes to use high-temperature copper slag as the heat carriers and catalyst for coal gasification, and CaO as the CO 2 adsorbent during the coal gasification reaction. In this way, the proportion of H 2 in the syngas gas can be increased, and the coal gasification reaction can be improved. In the experiment, the samples with different ratios were fully mixed, and then thermogravimetric experiment and gasification experiment were carried out. Through research, the following rules were found. The use of high-temperature copper slag as the heat source and catalyst in coal gasification can lead to a 20% increase in the final weight loss rate. Additionally, when CaO is used as the CO 2 adsorbent during the coal gasification reaction, a noticeable secondary weight loss occurs at around 600°C and can reach a maximum speed of 0.19%/min. The use of the C/S/CaO = 1/1/2 ratio can result in a maximum weight loss rate of 23%. Meanwhile, the C/S/CaO = 1/2/1 group has been shown to achieve a maximum weight loss speed of 0.5%/min, and the C/S/CaO = 1/1/1 group exhibits a maximum secondary weight loss speed of 0.32%/min. The samples after gasification experiment were analyzed by SEM, CaO produced clustered iron-based and porous structure on the surface of copper slag in gasification reaction. Based on the Coats-Redfern method, kinetics of gasification reaction is obtained, and the optimum fitting function is C2, mechanism functions didn't change with the variation of C/S/CaO. The research results suggest that CaO and copper slag can both enhance the coal gasification reaction. In addition, CaO is proven to be a more affordable and accessible CO2 adsorbent compared to other alternatives.

Physicochemical Properties of Coal Gasification Slag and Its Catalytic Effect on Gasification Reactivity of Petroleum Coke

In-Situ Experimental Study of Co2 Gasification of Char Particles on Molten Slag Surface

Effect of CaO-SiO2-FeO slag system on coal gasification reaction in CO2-Ar atmosphere and kinetic analysis

Characteristics and Catalytic Actions of Inorganic Constituents from Entrained-Flow Coal Gasification Slag

The gasification reactivity of unburned carbon present in gasification slag from entrained-flow gasifier

Effects of Molten Slag on Coal Gasification Reaction with CO2 at Elevated Temperature

Effect of coal slag on stability of petroleum coke water slurry

Catalytic effect of industrial waste carbide slag on pyrolysis of low-rank coal

The effect of CaO on coal gasification reaction with high-temperature copper slag as catalyst

Quantitative analysis of minerals of blended coal ash at high temperature and its influence on slagging

Investigation on carbide slag catalytic effect of Mongolian bituminous coal steam gasification process

Study on gasification reactivity of high sulfur petroleum coke and coal mixture

Progress in Physicochemical Properties of Ash/slag from Co-Gasification of Agroforestry Waste Biomass and Coal

Preparation of High Strength and Highly Reactive Coke by the Addition of Steel Slag

Investigation of the Characteristics of Catalysis Synergy During Co-Combustion for Coal Gasification Fine Slag with Bituminous Coal and Bamboo Residue

Research on the Application of Coal Gasification Slag in Soil Improvement

Experimental study on co-pyrolysis of petroleum coke and coals: Synergy effects and co-gasification reactivity

Effect of Purified Dust from CaC2 Production and Bottom Ashes/slags on Slagging Characteristic of Zhundong Coal Blend

Study on the Fragmentation Behaviors of Deposited Particles on the Molten Slag Surface and Their Effects on Gasification for Different Coal Ranks and Petroleum Coke

Effect of Adding Coal Ashes and Oxide Mixtures on CO 2 Gasification Reactivity of Petcoke at High Temperature

Catalytic pyrolysis of tar-rich coal for coal tar to light oil with catalysts of modified granulated blast furnace slag