Layer Thickness-Dependent Hardness and Strain Rate Sensitivity of Cu–Al/Al Nanostructured Multilayers
Ya-Qiang Wang,Zhao-Qi Hou,Jin-Yu Zhang,Xiao-Qing Liang,Gang Liu,Guo-Jun Zhang,Jun Sun
DOI: https://doi.org/10.1007/s40195-016-0372-7
2016-01-01
Acta Metallurgica Sinica (English Letters)
Abstract:Cu–Al/Al nanostructured metallic multilayers with Al layer thickness h Al varying from 5 to 100 nm were prepared, and their mechanical properties and deformation behaviors were studied by nanoindentation testing. The results showed that the hardness increased drastically with decreasing h Al down to about 20 nm, whereafter the hardness reached a plateau that approaches the hardness of the alloyed Cu–Al monolithic thin films. The strain rate sensitivity (SRS, m ), however, decreased monotonically with reducing h Al . The layer thickness-dependent strengthening mechanisms were discussed, and it was revealed that the alloyed Cu–Al nanolayers dominated at h Al ≤ 20 nm, while the crystalline Al nanolayers dominated at h Al > 20 nm. The plastic deformation was mainly related to the ductile Al nanolayers, which was responsible for the monotonic evolution of SRS with h Al . In addition, the h Al -dependent hardness and SRS were quantitatively modeled in light of the strengthening mechanisms at different length scales.