Abstract:The growing technological demand for high-efficiency direct methanol fuel cells (DMFCs) drives the exploration of catalysts with improved catalytic performance. Conventional pure Pt with good catalytic activity for methanol oxidation reaction (MOR) have been applied in the DMFCs for several decades, while their CO tolerance still needs to be further enhanced. Formation of nanoporous structure with a high specific surface area is an effective way to increase the catalytic efficiency by providing more active sites. Alloying suitable Fe and Ru into Pt is promising for the improvements of both catalytic activity and anti-CO poisoning. In this work, the nanoporous alloys have been fabricated by dealloying Fe65Pt10-xRuxB25 (x=0, 2, 4, atomic fraction, %) melt-spun alloy ribbons in 0.1 mol/L H2SO4 solution, and the phase structures, morphologies, chemical compositions, and magnetic properties of the melt-spun ribbons and nanoporous alloys were characterized by XRD, TEM, SEM, EDS, XPS and VSM, respectively. The electrocatalytic properties for MOR of the nanoporous alloys were examined by cycle voltammetry in 0.5 mol/L H2SO4+1.0 mol/L CH3OH solution. The results reveal that all melt-spun ribbons are fully amorphous, and nanoporous (Pt, Ru)Fe with a single-fcc phase can be obtained after dealloying. The nanoporous (Pt, Ru)Fe dealloyed from x=0 and 2 precursors possess a similar fine bicontinuous ligament/channel structure with average pore diameter and ligament size of 6 similar to 7 and 7 similar to 8 nm, respectively. Cracks can be found on the surficial nanoporous architecture for the nanoporous PtRuFe obtained from the x=4 alloy. With enriching of Ru, the oxidation peak potential of the nanoporous alloys exhibits a negative shift, and the ratio (j(f)/j(b)) of the peak current density in the forward scan (j(f)) to that in the backward scan (j(b)) increases gradually. The j(f) and j(f)/j(b) for the nanoporous PtRuFe dealloyed from the x=2 alloy is 0.87 mA/cm(2) and 4.6, which are 1.7 and 2.7 times of those for the nanoporous PtFe, respectively, indicating the superior electrocatalytic activity for MOR and CO tolerance in comparison with the binary PtFe alloy. The improvement in electrocatalytic performance after Ru addition can be attribute to the combination of Pt/Ru bifunctional mechanism and weakened Pt-COads adsorption energy. In addition, the nanoporous PtRuFe alloys also exhibit ferromagnetic characteristic with saturation magnetization values of 0.41 similar to 0.42 T, which can be easily separated and recycled in the practical applications. This work paves the way for the development of high-performance MOR electrocatalyst.

Hierarchical Nanoporous Ptfe Alloy With Multimodal Size Distributions And Its Catalytic Performance Toward Methanol Electrooxidation

Highly Active Nanoporous Pt-based Alloy As Anode and Cathode Catalyst for Direct Methanol Fuel Cells

Double Nanoporous Structure with Nanoporous PtFe Embedded in Graphene Nanopores: Highly Efficient Bifunctional Electrocatalysts for Hydrogen Evolution and Oxygen Reduction

Nanoporous PtFe surface alloy architecture for enhanced methanol electro-oxidation

Facile Synthesis of Ptcu3 Alloy Hexapods and Hollow Nanoframes As Highly Active Electrocatalysts for Methanol Oxidation

Facile Synthesis of Ternary PtPdCu Alloy Hexapods As Highly Efficient Electrocatalysts for Methanol Oxidation

Tuning Surface Structure of Pd3Pb/PtnPb Nanocrystals for Boosting the Methanol Oxidation Reaction

Nanoporous PtCo Surface Alloy Architecture with Enhanced Properties for Methanol Electrooxidation.

Pt Nanoparticles Dispersed on Ni/C Nanoflowers As Stable Electrocatalysts for Methanol Oxidation and Oxygen Reduction

Electronic and Coordination Effect of PtPd Nanoflower Alloys for the Methanol Electrooxidation Reaction

Platinum Decorated Hierarchical Porous Structures Composed of Ultrathin Titanium Nitride Nanoflakes for Efficient Methanol Oxidation Reaction

Structurally ordered PtFe intermetallic nanocatalysts toward efficient electrocatalysis of methanol oxidation

The in Situ Etching Assisted Synthesis of Pt-Fe-Mn Ternary Alloys with High-Index Facets As Efficient Catalysts for Electro-Oxidation Reactions

Fabrication of Nanoporous PtRuFe by Dealloying Amorphous Fe(Pt, Ru)B Ribbons and Their Methanol Electrocatalytic Properties

Fe2O3@FeP Core-Shell Nanocubes/c Composites Supported Irregular PtP Nanocrystals for Enhanced Catalytic Methanol Oxidation

Synthesis of Intermetallic FePtPd Nanoparticles and Their Enhanced Catalysis for Electro-Oxidation of Methanol

Tailoring the electronic structure of PtNi nanoalloy for boosting methanol electro-oxidation reaction

2H‐au Nanosheet‐Templated Growth of PdFe for Electrocatalytic Methanol Oxidation

One-step Synthesis of Porous PtNiCu Trimetallic Nanoalloy with Enhanced Electrocatalytic Performance Toward Methanol Oxidation

Efficient and Stable PtFe Alloy Catalyst for Electrocatalytic Methanol Oxidation with High Resistance to CO

Highly Graphitized Carbon-Wrapped PtFeCo Alloy with Enhanced Durability and Activity Toward Methanol Electro-Oxidation