Abstract:Porous hollow silica particles possess promising applications in many fields, ranging from drug delivery to catalysis. From the synthesis perspective, the most challenging parameters are the monodispersity of the size distribution and the thickness and porosity of the shell of the particles. This paper demonstrates a facile two-pot approach to prepare monodisperse porous-hollow silica particles with uniform spherical shape and well-tuned shell thickness. In this method, a series of porous-hollow inorganic and organic-inorganic core-shell silica particles were synthesized via hydrolysis and condensation of 1,2-bis(triethoxysilyl) ethane (BTEE) and tetraethyl orthosilicate (TEOS) in the presence of hexadecyltrimethylammonium bromide (CTAB) as a structure-directing agent on solid silica spheres as core templates. Finally, the core templates were removed via hydrothermal treatment under alkaline conditions. Transmission electron microscopy (TEM) was used to characterize the particles′ morphology and size distribution, while the changes in the chemical composition during synthesis were followed by Fourier-transform infrared spectroscopy. Single-particle inductively coupled plasma mass spectrometry (spICP-MS) was applied to assess the monodispersity of the hollow particles prepared with different reaction parameters. We found that the presence of BTEE is key to obtaining a well-defined shell structure, and the increase in the concentration of the precursor and the surfactant increases the thickness of the shell. TEM and spICP-MS measurements revealed that fused particles are also formed under suboptimal reaction parameters, causing the broadening of the size distribution, which can be preceded by using appropriate concentrations of BTEE, CTAB, and ammonia.

One-Pot Synthesis of Polyhedron-Like Hollow Aluminosilicate with Mesoporous Shells

One-pot Template-Free Synthesis of Mesoporous Boehmite Core–shell and Hollow Spheres by a Simple Solvothermal Route

Template-assisted Synthesis of Mesoporous LiAlO2 Hollow Spheres with High Surface Area

Synthesis of Porous Hollow Organosilica Particles with Tunable Shell Thickness

A Facile Route to Synthesis of Hollow SiO2/Al2O3 Spheres with Uniform Mesopores in the Shell Wall

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Anionic Surfactants Templating Route for Synthesizing Silica Hollow Spheres with Different Shell Porosity

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

One-Pot Synthesis and Formation Mechanism of Hollow ZSM-5.

Synthesis of Hollow Spheres with Mesoporous Silica Nanoparticles Shell

Synthesis of Stable Hollow Spheres of Si/Al Composite Oxide with Controlled Pore Size in the Shell Wall

Efficient Synthesis of Hollow Silica Microspheres Useful for Porous Silica Ceramics

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Hollow mesoporous aluminosilica spheres with perpendicular pore channels as catalytic nanoreactors

One-Pot Synthesis of Catalytically Stable and Active Nanoreactors : Encapsulation of Size-Controlled Nanoparticles within a Hierarchically Macroporous Core

One-step Direct Synthesis of Mesoporous Aluminosilicates Al-SBA-15 with Cage-Like Macropores by Using Micrometer-Sized Aluminum Balls

Salt-templated Synthesis and Morphological Control of Monodisperse Hollow Mesoporous Structures

A Unique Transformation Route for Synthesis of Rodlike Hollow Mesoporous Silica Particles