Abstract:Manganese oxides with desired structure are controllably obtained through annealing MnCO3 precursors with required structures. The structures of MnCO3 precursors are determined by a "mesocrystal formation" process in an ionic liquid system of a choline chloride/urea (CU) mixture. Without addition of surfactants, only CU solvent and manganese chloride are needed in the reaction system, in which the CU acts as reaction medium as well as control agent for particle growth. A shape transformation of MnCO3 particles from well-defined rhombohedral mesocrystals to ellipsoidal polycrystal ensembles, and to nanoparticulate aggregates is observed when heating the reaction system for 4 h at 120, 150, and 180 °C, respectively. With a longer aging time at 120 °C, etching and disassembly of MnCO3 mesocrystals happened. The correlation between the microstructure and the underlying formation mechanism is highlighted. Porous and nanowire-like MnO(x) nanostructures are obtained through a facile thermal conversion process from the diverse MnCO3 precursors, which are demonstrated as effective and efficient adsorbents to remove organic waste (e.g. Congo red) from water. Significantly, the nanowire-like MnO(x) nanostructures obtained by annealing the MnCO3 mesocrystals at 300 °C for 4 h can remove about 95% Congo red in waste water at room temperature in only one minute, which is superior to the reported hierarchical hollow nanostructured MnO2.

Synthesis of Mn2O3 Homogeneous Core/Hollow-Shell Structures with Excellent Adsorption Performance.

Microscale Mn2O3 Hollow Structures: Sphere, Cube, Ellipsoid, Dumbbell, and Their Phenol Adsorption Properties

Fabrication of Γ-Mno2/α-mno2 Hollow Core/shell Structures and Their Application to Water Treatment

General Synthesis of Metal Oxide Hollow Core–shell Microspheres As Anode Materials for Lithium-Ion Batteries and As Adsorbents for Wastewater Treatment

Double‐Shelled Mn2O3 Hollow Spheres and Their Application in Water Treatment

Synthesis of the Porous Mn<sub>2</sub>O<sub>3</sub> Microsphere and Mn<sub>2</sub>O<sub>3</sub>@SiO<sub>2</sub> Core-Shell Nanostructure by a Facile Method

Synthesis of Porous and Hollow Microspheres of Nanocrystalline Mn2O3

Synthesis of poly(methacrylic acid)-manganese oxide dihydroxide/silica core-shell and the corresponding hollow microspheres

Rapid Synthesis of Hollow Structured MnO2 Microspheres and Their Capacitance

Hydrothermal synthesis of hierarchical core–shell manganese oxide nanocomposites as efficient dye adsorbents for wastewater treatment

Design and Preparation of MnO2/CeO2-MnO2 Double-Shelled Binary Oxide hollow spheres and Their application in CO oxidation.

Controlled Preparation of MnO2 Hierarchical Hollow Nanostructures and Their Application in Water Treatment

Morphology-controllable Synthesis of MnO2 Hollow Nanospheres and Their Supercapacitive Performance

Endowing Manganese Oxide with Fast Adsorption Ability Through Controlling the Manganese Carbonate Precursor Assembled in Ionic Liquid.

Shape-Controlled Synthesis of MnO<sub>2</sub>Nanostructures with Enhanced Electrocatalytic Activity for Oxygen Reduction

Shape-controlled Synthesis of Hierarchical Hollow Urchin-Shape Α-Mno2 Nanostructures and Their Electrochemical Properties

One-pot facile synthesis of hierarchical hollow microspheres constructed with MnO2 nanotubes and their application in lithium storage and water treatment

Templated synthesis of hierarchically porous manganese oxide with a crystalline nanorod framework and its high electrochemical performance

Synthesis and Characterization of Hierarchically Structured Mesoporous Mno2 and Mn2o3

Hollow MnCo2O4 submicrospheres with multilevel interiors: from mesoporous spheres to yolk-in-double-shell structures.

Synthesis Of Porous, Hollow Metal Mco3 (M=Mn, Co, Ca) Microstructures And Adsorption Properties Thereof