Synthesis of TiO2/Pt/TiO2 Multilayer Films Via Radio Frequency Magnetron Sputtering and Their Enhanced Photocatalytic Activity

Chao Ma,Wen Dong,Liang Fang,Fengang Zheng,Mingrong Shen,Zhenlin Wang

DOI: https://doi.org/10.1016/j.tsf.2012.04.011

IF: 2.1

2012-01-01

Thin Solid Films

Abstract:TiO2/Pt/TiO2 (TPT) multilayered films with different thicknesses of Pt layers from about 0.75 to 12nm were prepared by radio frequency magnetron sputtering method. The as-prepared films were characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy, UV–visible diffuse reflectance spectroscopy, and photoluminescence spectroscopy. The photocatalytic activity of the samples was evaluated by the photocatalytic decolorization of methyl blue aqueous solution under ultraviolet light irradiation. The photocatalytic activities of all TPT multilayer films were higher than that of the pure TiO2 films. When Pt thickness was increased to 3nm, the measured photocatalytic activity of the TPT film was highest, and exceeded that of the pure TiO2 films by a factor of more than three times. Such enhancement was ascribed to the presence of Pt layer, which inhibits the recombination of the photogenerated charge and carriers, as well as modifies the crystallinity of the TiO2 top layer.