Abstract:Melamine–formaldehyde resin-microencapsulated ammonium polyphosphate (MFAPP) was prepared by in situ polymerization using melamine–formaldehyde (MF) resin as the shell material. MFAPP was characterized by X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM), which confirmed its successful fabrication. MFAPP was further introduced to prepare rigid polyurethane foam/microencapsulated ammonium polyphosphate composites (RPUF/MFAPP). The flame retardancy, water resistance, physical properties, and thermal stability of RPUF/MFAPP were compared with virgin RPUF and RPUF/APP composite. RPUF/MFAPP30 possessed excellent flame retardancy. Even after immersion in water for 15 days, RPUF/MFAPP30 achieved V-1 rating in UL-94 test with limiting oxygen index (LOI) of 21.3 vol%, which was better than that of RPUF/APP30 with equivalent APP loading. The compressive strength of RPUF/MFAPP30 was 0.295 MPa, which was 13.5% higher than that of RPUF/APP30. Thermogravimetric analysis-Fourier transform infrared spectroscopy (TGA-FTIR) was applied to investigate gaseous products of the decomposition process for RPUF/APP and RPUF/MFAPP. It was found that the intensities of CO<sub>2</sub>, isocyanate compounds, and CO for RPUF/MFAPP were lower than the values for RPUF/APP, indicating superior fire safety of RPUF/MFAPP. SEM and Raman spectra confirmed that RPUF/MFAPP30 possessed more compact char residue with higher thermal resistance, which was thus better able to inhibit mass and heat transmission in combustion. Consequently, a possible gas–solid flame-retardant mechanism of the RPUF/MFAPP composite was proposed.

Properties of flame retardant polypropylene with melamine-formaldehyde resin microencapsulated ammonium polyphosphate

Effect of the Surface Modification of Ammonium Polyphosphate on the Structure and Property of Melamine–formaldehyde Resin Microencapsulated Ammonium Polyphosphate and Polypropylene Flame Retardant Composites

Microencapsulation of Ammonium Polyphosphate: Preparation, Characterization, and Its Flame Retardance in Polypropylene

Microencapsulation of Ammonium Polyphosphate in Different Volume Ratios of Water and Alcohol and Its Flame Retardance in Polypropylene

Microencapsulated Ammonium Polyphosphate with Urea–melamine–formaldehyde Shell: Preparation, Characterization, and Its Flame Retardance in Polypropylene

Flame Retardation of PP/EPDM Composites Containing Ammonium Polyphosphate and Its Microcapsules

Microencapsulation of Ammonium Polyphosphate with PVA–melamine–formaldehyde Resin and Its Flame Retardance in Polypropylene

Water Resistance, Thermal Stability, and Flame Retardation of Polypropylene Composites Containing a Novel Ammonium Polyphosphate Microencapsulated by UV-curable Epoxy Acrylate Resin

Synthesis of a Novel Intumescent Flame Retardant and Its Flame Retardancy in Polypropylene

Crystallization Morphology and Behavior of Polypropylene Composites Containing Microencapsulated Flame Retardant

Study on Microencapsulated Halogen-free Intumescent Flame-Retardant Polypropylene

Microencapsulated Ammonium Polyphosphate with Glycidyl Methacrylate Shell: Application to Flame Retardant Epoxy Resin

Influence of Ammonium Polyphosphate Microencapsulation on Flame Retardancy, Thermal Degradation and Crystal Structure of Polypropylene Composite

Mechanical property improvement and fire hazard reduction of ammonium polyphosphate microencapsulated in rigid polyurethane foam

Effect of Microencapsulated APP by Epoxy Resin on Property of Flame-Retardant Polypropylene

Preparation and Characterization of Double Shell Microencapsulated Ammonium Polyphosphate and Its Flame Retardance in Polypropylene

Preparation of melamine–formaldehyde resin-microencapsulated ammonium polyphosphate and its application in flame retardant rigid polyurethane foam composites

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

Modified Ammonium Polyphosphate and Its Application on Polypropylene

Effect of Microencapsulation on Thermal Properties and Flammability Performance of Epoxy Composite

Microencapsulated Ammonium Polyphosphate with Polyurethane Shell: Application to Flame Retarded Polypropylene/Ethylene-Propylene Diene Terpolymer Blends