Structure Characterization and Electrode Properties of AB5 Hydrogen Alloy Suitable for Wide-Temperature Application

Ni Chengyuan,Zhou Huaiying,Wang Zhongmin,Ou Qiju,Ma Yufei

DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.02.011

2012-01-01

Abstract:Mm(NiCoAlMn) 5 alloy was fabricated in arc-melting furnace under argon atmosphere, and its electrochemical properties, including activation, discharge capacity, cycle stability and high rate discharge (HRD), were investigated using simulated battery. The results indicated that the as-prepared alloy belonged to AB 5 type structure, its hydrogen capacity was 1.38% (mass fraction) at 303 K, and the enthalpy change in the formation of hydride was 32.36 kJ·mol -1 H 2. The electrochemical properties of the alloy electrodes were mainly affected by temperature. Pre-activation for these samples under room temperature enhanced their low-temperature properties. The maximum discharge capacity of the alloy electrode reached 336 mAh·g -1 at 238 K if an additional pre-activation process was applied, which was evidently higher than that without pre-activation, 25 mAh·g -1. The high rate dischargeability fluctuated with increasing test temperature. When tested at 273 and 303 K, both the alloy electrodes exhibited good high rate dischargeabilities, which were more than 80% while the discharge current density of less than 3 C. However, the high rate dischargeability decreased rapidly at 238 K, which was only 10% at discharge current density 1C. A better performance was observed in 273 K, where 340 mAh·g -1 of maximum capacity, 86% of high rate discharge (HRD 300) was obtained. Cyclic voltammetry tests showed that it had a good linear relationship between the oxidation peak current (I P) and the square of voltage scanning speed (ν 1/2), suggesting that electrode reaction was controlled by diffusion process. The hydrogen diffusion coefficient decreased sharply with decreasing temperature, followed by a poor HRD performance at low temperature. The activation energy for hydrogen diffusion in Mm(NiCoAlMn) 5 alloy electrodes was calculated to be 10.56 kJ·mol -1H 2, using the Arrhenius equation.