Biomimetic Synthesis of Aragonite Nanorod Aggregates with Unusual Morphologies Using A Novel Template of Natural Fibrous Proteins at Ambient Condition

Zengqiong Huang,Gangsheng Zhang

DOI: https://doi.org/10.1021/cg201293f

IF: 4.01

2012-01-01

Crystal Growth & Design

Abstract:Biomimetic synthesis of calcium carbonate has been studied for decades in order to understand the biomineralization process. However, to date, it is still difficult to obtain pure aragonite by transformation of amorphous calcium carbonate (ACC) at room temperature. Herein, we obtained almost pure aragonite nanorod aggregates (ANA) with unusual morphologies via transformation of ACC at ambient conditions using a novel fibrous protein K58 from bivalve Siliqua radiata ligament as the template. We found that nanorods are formed initially as ACC containing disordered aragonite nanocrystals, which then evolve into oriented attached nanocrystals coated with minor ACC, and finally into aragonite single crystals. Further analysis reveals K58 is homologous to type II cytoskeletal 1 and type I cytoskeletal 9, with many acidic amino acid residues. It should be the carboxyl groups of these residues, which have short-range order similar to aragonite lattice, control short-range order ACC formation, resulting in the preferential transformation of ACC into aragonite. This article provides some valuable information for better understanding of aragonite crystal growth and biomineralization process; it also highlights the role of biomacromolecule in the formation of aragonite fibers in bivalve ligaments.