Synthesis and Photoluminescence Properties of Eu3+-doped Γ-Ca3(po4)2

Weihong Xue,Shuangmeng Zhai,Haifei Zheng

DOI: https://doi.org/10.1016/j.matchemphys.2012.01.031

IF: 4.778

2012-01-01

Materials Chemistry and Physics

Abstract:Eu3+-doped (1% and 3%) γ-Ca3(PO4)2 was synthesized by high-pressure and high-temperature experimental method and the samples were characterized by X-ray diffraction. The luminescence properties of samples were investigated by emission and excitation spectra. The excitation spectra of Eu3+-doped γ-Ca3(PO4)2 showed that samples were mainly attributed to Eu3+–O2− charge-transfer band at 270nm, and some sharp lines were also attributed to Eu3+ f–f transitions in near-UV regions with the strongest peaks at 395nm. Under the 395nm excitation, the intense red emission peak at 611nm was observed. The strongest line (395nm) in excitation spectra of those phosphors matched well with the output wavelength of UV InGaN-based light-emitting diodes (LEDs) chip. The luminescent properties suggested that Eu3+-doped γ-Ca3(PO4)2 might be regarded as a potential red phosphor candidate for near-UV LEDs.