Abstract:Hollow-structured SiO2, which comprises a void space inside a distinct shell with its intriguing physicochemical properties and huge potential, has been widely applied in many methanation catalysts. However, the common methods for preparing SiO2 hollow microspheres are cumbersome and time consuming. Highly uniform hollow nanoflowers, silica (SiO2) nanospheres with different sizes, were synthesised through a rapid, time-saving method known as flash nanoprecipitation. An assembling particle mechanism of the hollow structure of Mo–polydopamine complex was established and tetraethyl orthosilicate underwent uniform hydrolysis on the surface of the hierarchical structure. Spherical SiO2 samples with different morphologies were prepared as catalyst carriers, and Ni-based methanation catalysts were prepared using an impregnation method. Ni particles with size of 3 nm were successfully attached to the surface of MoDo–H–SiO2, while the particle sizes of Ni on CTS–MoDo–H–SiO2 was 7 nm. The small particles (3 nm) were found to significantly increase in size (20–50 nm), decrease by 90% in stability test with a weight hourly space velocity (WHSV) of 26,000 mL.g−1.h−1, which is detrimental to catalyst stability. However, the medium sized particles (7 nm) remained confined via a suitable interaction involving the support, thus displaying enhanced stability, with 100% CO conversion at 250 °C and no obviously decrease in stability test Although more active sites can be provided with smaller active metals, catalysts with small sized particles deactivate faster and to a larger extent than catalysts with medium sized particles. Thus, the smaller the particle size of the active component, the worse the stability.

Simultaneous Pore Enlargement and Introduction of Highly Dispersed Fe Active Sites in MSNs for Enhanced Catalytic Activity

Preparation and Catalytic Activity of Manganese Doped Mesoporous Silica Nanoparticles with Large Pore Size

ZIF-8 derived Fe-N coordination moieties anchored carbon nanocubes for efficient peroxymonosulfate activation via non-radical pathways: Role of FeN<sub>x</sub> sites

Combining two active states of FeOx in-situ in molecular sieve to deliver enhanced catalytic activity via creating special configuration and synergy

Construction of large-aperture mesoporous silica spheres supported polyoxometalate heterogeneous catalysts and their high-efficiency for the ultra-deep desulfurization

A Simple Co-Impregnation Route to Load Highly Dispersed Fe(III) Centers into the Pore Structure of SBA-15 and the Extraordinarily High Catalytic Performance

Magnetic Fe/N-codoped carbon derived from modified Fe-base MOFs: Synergism of multiple active sites for peroxymonosulfate activation

Synthesis and Characterization of Fe,Cr or Sn-MSU-X and Catalytic Applications

Enabling synchronous activation of inner-core and mesoporous outer-shell of monodispersed Fe3O4@SiO2 by in-situ implanted MnO to synergistically deliver enhanced catalytic activity

Multifunctional Mesoporous Composite Microspheres with Well-Designed Nanostructure: a Highly Integrated Catalyst System.

Templated Silica with Increased Surface Area and Expanded Microporosity: Synthesis, Characterization, and Catalytic Application

Nanoscale gold intercalated into mesoporous silica as a highly active and robust catalyst.

Synergistically enhancing Fenton-like degradation of organics by in situ transformation from Fe3O4 microspheres to mesoporous Fe, N-dual doped carbon

Coupled Surface-Confinement Effect and Pore Engineering in a Single-Fe-Atom Catalyst for Ultrafast Fenton-like Reaction with High-Valent Iron-Oxo Complex Oxidation.

Facile tuning Non-radical/Radical oxidation by nitrogen doping on Fe-S doped carbonaceous catalysts for peroxymonosulfate activation

Mesoporous ferrosilicates with high content of isolated iron species synthesized in mild buffer solution and their catalytic application

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Integration of Pd nanoparticles with engineered pore walls in MOFs for enhanced catalysis

Facile Synthesis of Fe-Loaded Mesoporous Silica by a Combined Detemplation−Incorporation Process Through Fenton’s Chemistry

Up-scaled Synthesis of Flower-Like SiO2 Microspheres Via Continuous Flash Nanoprecipitation and Their Application As a Catalyst Support

Magnetically separable mesoporous silica nanocomposite and its application in Fenton catalysis