Abstract:Nearly monodispersed CaWO4 hollow microspheres with controlled diameters were successfully prepared by a facile one-step hydrothermal method using CaCl2, Na2WO4, and sodium dodecyl sulfate (SDS) as the starting reaction reagents and distilled water as solvent. The crystal structure, morphology, macroporous and photoluminescence properties of the as-synthesized products are characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected-area electron diffraction, nitrogen adsorption-desorption isotherm technique, and fluorescence spectrometer. The hollow microspheres have an average diameter of 2.2 mu m and hollow interior of 0.5-1 mu m. The shell is consisting of numerous nanoparticles 45 nm in diameter. The effects of SDS amount, pH value, concentrations of reaction reagents, and reaction durations have been studied systematically. The results indicate that a certain SDS amount plays a key important role in the final formation of hollow microspheres. It is also found that the average diameters of the hollow spheres can also be tuned by increasing the SDS amount in the range of 0.2-1 g into the reaction system. Based on the detailed investigation on the influences of experimental parameters, the formation mechanism of the hollow interiors by a SDS-induced Ostwald ripening process is proposed for the CaWO4 hollow microspheres. The B runauer-Emmett-Teller (BET) surface areas and pore volume of the CaWO4 hollow microspheres are 14.4 m(2)/g and 0.087 cm(3)/g, respectively. Furthermore, photoluminescence spectrum of the CaWO4 hollow microspheres reveals a strong and broadband from 350 to 450 nm with an emission peak at 413 nm originating from the WO42- groups. This Ostwald ripening process could open novel and efficient pathway for the preparation of ternary metal oxides with hollow interiors.

Hydrothermal synthesis of quasi-monodisperse AWO 4 (A = Ca, Sr, and Ba) microspheres

Preparation, Structural And Optical Properties Of Awo(4) (A = Ca, Ba, Sr) Nanofilms

Environmentally Friendly Aqueous Solution Synthesis of Hierarchical Cawo4 Microspheres at Room Temperature

Synthesis of Cawo4 and Cawo4:Eu Microspheres by Precipitation

Hydrothermal Synthesis and Luminescence Properties of Monodisperse BaWO4:Eu3+ Submicrospheres

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Nearly Monodisperse Tungstate MWO4 Microspheres (M = Pb, Ca): Surfactant-Assisted Solution Synthesis and Optical Properties

Hydrothermal Synthesis of PbWO4 Uniform Hierarchical Microspheres

Mono-Disperse CaWO4 Microsphere with Hierarchical Structures: Room Temperature Synthesis and Its Optical Properties

Surfactant-assisted synthesis of single crystal BaWO4 octahedral microparticles

Synthesis of Urchin-Like Cdwo4 Microspheres Via A Facile Template Free Hydrothermal Method

Shape-controlled of CaWO4 microcrystals by self-assembly of nanocrystals via a simple sonochemical method

Controllable Synthesis of Hierarchical Nanostructures of Cawo4 and Srwo4 Via A Facile Low-Temperature Route

Hydrothermal synthesis and luminescence properties of uniform BaMoO 4:Ln 3+ (Ln = Eu, Tb, Dy, and Sm) microspheres

A General Approach to Monodisperse Perovskite Microspheres

Microsphere Morphology Tuning and Photo-Luminescence Properties of Monoclinic Y2wo6

Controlled Synthesis of Calcium Tungstate Hollow Microspheres via Ostwald Ripening and Their Photoluminescence Property

Simple Room-Temperature Mineralization Method to SrWO4 Micro/Nanostructures and Their Photocatalytic Properties

Surfactant-assisted hydrothermal synthesis of Eu(3+)-doped white light hydroxyl sodium yttrium tungstate microspheres and their conversion to NaY(WO(4))(2).

Fabrication, Characterization, and Luminescence Properties of Highly Uniform PbWO4:Ln3+ (ln = Tb, Eu, Dy, and Sm) Hierarchical Microspheres

Surfactant-Assisted Hydrothermal Synthesis, Physical Characterization, and Photoluminescence of Pbwo4