Biocompatibility of the compound pattern of extracellular matrix and temperature dependent hydrogel with bladder smooth muscle cells
Yao Y,Zhang J,Fang L,Ye DF,Peng JP,Li Q
2007-01-01
Abstract:AIM:To evaluate the biocompatibility of compound pattern of extracellular matrix (ECM) and temperature-sensitive hydrogel (HG) in vitro to the bladder smooth muscle cells (SMCs). METHODS: The study was finished in the Laboratory of Urology in the Renmin Hospital of Wuhan University from February to May in 2005.①There were 4 groups in this experiment: SMCs were cultured in ECM (group A), in the ECM/HG compounds materials (group B) and on the plastic surfaces as a negative control (group C) respectively. There was no cell culture fluid in group D, which played as a blank control.②The compound materials were moistened with culture fluid and inoculated with 50 μL rabbit bladder SMC suspension (1×108 L-1) at third passage.③Two days after culturing, cells and the compound materials were observed by phase contrast microscopy and scanning electron microscope to assess cell adhesion, proliferation, and growth. At the 5th and 10th days, the cells of group A and group B were counted to observe the cell adhesion. Cell activity was detected with MTT assay at 1, 3, 5 and 7 days after culture. RESULTS: ①Histologically, the ECM/HG compounds appeared as a net-like and red-stained construction with enough meshes and without any cellular fragments. Six hours after implantation, cells were observed to adhere on the compounds and extend spuriously along the fibers 12 hours later. Three days later, the adhesive cells were increased in number and proliferated obviously.②Under scanning electron microscope, the proliferated cells adhered closely on materials, and pseudopodia extended along fibers, even some ECMs were secreted.③The SMC adhesion was notable on the ECM and the compound materials as well, the adhesion rate was 87.6% and 96.7%, respectively.④The cell activity in group B and group C was significantly higher than that of group A (P < 0.05, 0.01). At 1, 3, 5 days after culture, the cell activity of group B was lower than that of group C and higher at 7 days, with the significant differences (P < 0.05, 0.01). CONCLUSION: ECM/HG compounds materials benefit for the cell adhesion and growth, appear great biocompatibility, and accelerate the tissue regeneration, which confirm that it will be an ideal tissue engineering scaffold.