Abstract:The spallation of the concrete slabs or walls resulting from contact detonation constitutes risk to the personnel and equipment inside the structures because of the high speed concrete fragments even though the overall structures or structural members are not destroyed completely.Correctly predicting the damage caused by any potential contact detonation can lead to better for-tification design to withstand the blast loadings.It is therefore of great significance to study the mechanism involved in the spallation of concrete slabs and walls.Existing studies on this topic of-ten employ simplified material models and 1D wave analysis,which cannot reproduce the realistic response in the spallation process.Numerical simulations are therefore carried out under different contact blast loadings in the free air using LS-DYNA.Sophisticated concrete and reinforcing bar material models are adopted,taking into account the strain rate effect on both tension and com-pression.The erosion technique is used to model the fracture and failure of materials under tensile stress.Full processes of the deformation and dynamic damage of reinforced concrete （RC） slabs and plain concrete slabs are thus observed realistically.It is noted that with the increase of quantity of explosive,the dimensions of damage crater increase and the slabs experience four different damage patterns,namely explosive crater,spalling,perforation,and punching.Comparison be-tween the simulation results of plain concrete slabs and those of RC slabs show that reinforcing bars can enhance the integrity and shearing resistance of the slabs to a certain extent,and mean-while attenuate the ejection velocity and decrease the size of the concrete fragments.Therefore,optimizing reinforcement arrangement can improve the anti-spallation capability of the slabs and walls to a certain extent.

Research on the dynamic response of fully clamped plate to explosive loading

Investigation of dynamic response of brittle materials under high-rate loading

Numerical simulation of the disk fragment impacting resistance of plate target

Anisotropic Dynamic Damage and Fragmentation of Rock Materials under Explosive Loading

Penetration of Disk Fragments Following Impact on Thin Plate

Double blast loadings of clamped square steel plates

Dynamic Response Mechanism of Thin-Walled Plate under Confined and Unconfined Blast Loads

Influence of Explosive Shape on the Response of Steel Plates under Blast Loading

Numerical Simulation of Dynamic Response of Steel Plate Subjected to Multiple Underwater Explosions

Computer Simulation of Dynamic Brittle Damage Process in Arch Dam Due to Blast Load

Damage Mechanism Of Reinforced Concrete Slab Under Internal Blast Loading

PREDICTION OF DEBRIS LAUNCH VELOCITY OF REINFORCED CONCRETE SLAB SUBJECTED TO INTERNAL BLAST LOADING

Numerical Simulation of Blast Loads and Dynamic Response of Reinforced Concrete Slab Subjected to Close-in Explosion

Dynamic Analysis of Structural Columns Subjected to Impulsive Loading

Centrifuge Experiment and Numerical Analysis of an Air-Backed Plate Subjected to Underwater Shock Loading

Spallation Mechanism of RC Slabs under Contact Detonation

Numerical Simulation of the Effect of Blast Shock Wave on Target Plate

Plastic Deformation of Metal Tubes Subjected to Lateral Blast Loads

Macroscopic Dynamic Response and Microscopic Damage Formation Analysis of Steel Plates with Different Explosive Distances

Blast responses of steel stiffened panels subjected to plane shock waves

An analytical method for evaluating the dynamic response of plates subjected to underwater shock employing Mindlin plate theory and Laplace transforms