Abstract:Three types of interlayers named Hafnium carbide (HfC) single-interlayer, SiC/HfC double-interlayer, and HfC-SiC/HfC double-interlayer were designed and fabricated on cemented carbide (WC-Co) to seek out the optimal coating structure for well-adhered diamond coatings. The phase composition, microstructure, adhesion and effectiveness in diamond coating adhesion of these interlayers were investigated and compared. The results showed that the HfC single-interlayer was a HfC-dominant nanostructured layer composed of HfC, Si, and SiC. The SiC/HfC and the HfC-SiC/HfC double-interlayers had an inner layer with a structure similar to the HfC single-interlayer. However, the former had a SiC-dominant outer layer, while the latter had a gradient HfC-SiC mixed outer layer. The double-interlayers possessed better adhesion and higher hardness than those of the HfC single-interlayer. This could be attributed to the introduction of SiC in the outer layer, which endowed the substrates with significantly enhanced microhardness and decreased TEC, closer to those of diamond coatings. After the subsequent CVD process, dense nanocrystalline diamond coatings with a thickness of similar to 5.0 mu m were deposited onto the double-interlayered substrates. The coatings possessed good adhesion. Between them, the diamond coating on the HfC-SiC/HfC double-interlayered substrate had better adhesion (HF1 similar to HF2) and lower residual stress (-1.7 GPa) than those of the coating on the SiC/HfC double-interlayered substrate. These experimental results provide a feasible way for fabrication of well-adhered diamond coating on WC-Co tools. (C) 2019 Elsevier B.V. All rights reserved.

Effect of Multilayer Technology on Surface Properties of Diamond Coated Silicon Carbide with Surface Defects

Friction and Wear Performances of Hot Filament Chemical Vapor Deposition Multilayer Diamond Films Coated on Silicon Carbide under Water Lubrication

Fabrication and Application of Smooth Composite Diamond Films

Investigation Of Technology Of Depositing Low Surface Roughness Diamond Thin Films On Cemented Carbides Inserts

Tribological and Cutting Behavior of Silicon Nitride Tools Coated with Monolayer- and Multilayer-Microcrystalline Hfcvd Diamond Films

Growth and optical properties of nanocrystalline/microcrystalline diamond multilayer films

Growth of Nanocrystalline Diamond Films on Co-Cemented Tungsten Carbide Substrates by Hot Filament CVD

Effect of the interfacial microstructure on hardness of multi-layer diamond coatings

Fabrication and characterization of diamond films on SiC substrate

Improvement Of Adhesive Strength And Surface Roughness Of Diamond Films On Co-Cemented Tungsten Carbide Tools

Improvement of Adhesive Strength and Surface Roughness of Diamond-Coated Thin Film Tools

Study on Comparative Experiments of Performance of Conventional and Nanocrystalline Diamond Film

Cutting performance and wear mechanism of multilayer diamond coated tools

Effect of Surface Morphology on the Frictional Behaviour of Hot Filament Chemical Vapour Deposition Diamond Films

A New Route to Fabricate High-Quality Double-Side-polished Freestanding Diamond Film

FABRICATION AND APPLICATION OF NANOCRYSTALLINE DIAMOND FILMS

Design and Fabrication of HfC, SiC/HfC and HfC-SiC/HfC Interlayers for Improving the Adhesion Between Diamond Coatings and Cemented Carbides

Enhancement of Impact Resistance of CVD Diamond Coating by Multilayer Strategy

CVD Process for Improving Mechanical Properties of HFCVD Diamond-coated Thin Film Tools

Improvement in the universality of high-performance CVD diamond coatings on different WC-Co substrates by introducing multilayered diamond/β-SiC composite

SIMULATION AND EXPERIMENTAL RESEARCH ON ADHESION ENHANCEMENT BETWEEN DIAMOND FILMS AND WC-Co SUBSTRATES BY EMPLOYING AMORPHOUS SiC INTERLAYER