Abstract:In this paper, a 3D finite element model is established in ABAQUS/Explicit based on a modified progressive damage model to study the dynamic mechanical response and damage development in cross-ply composite laminates subjected to low-velocity impact. The 3D Hashin criterion and the damage evolution model with the through-thickness normal stress component sigma(33) are applied to predict the infra-laminar damage initiation and evolution. The cohesive elements with the bilinear traction-separation relationship are inserted between layers to predict the inter-laminar delamination induced by impact loading. A user-material subroutine VUMAT involving the modified progressive damage del of intra-laminar and inter-laminar damage is coded and implemented in the finite element package ABAQUS/Explicit. The numerical results of three different impact energies (7.35, 11.03 and 14.70 J) are analyzed by the impact force-time, force-displacement and energy-time histories curves as well as different damage modes. The respectable relationship between numerical simulation and experimental result indicates that the proposed modified method is more suitable for low-velocity impact on composite laminates under different impact energies than the previous method without sigma(33). Moreover, the effects of S-mt and S-mc on global mechanical response and local damage predictions for laminates are discussed in detail. It can be concluded that both of the coefficients should be adopted between 0.93 and 0.96 when using this damage model to simulate composite laminates under low-velocity impact.

Numerical simulation of compressive residual strength for damaged composite laminates

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Damage Analysis of Composite Laminate with Large Open-hole under Compression Using 3D Strain Progressive Damage Theory

Exploration of Several Influence Factors of Low-Velocity Impact Damage on Composite Laminates

Advance of Study on Residual Compressive Strength of Damaged Composite Laminates

Compressive Experiment and Damage Simulation of A Composite Structure with Ply Drop-Off

Finite Element Analysis of a Modified Progressive Damage Model for Composite Laminates under Low-Velocity Impact

Experimental and numerical simulation study on Near-edge/On-edge Low-Velocity impact and residual compressive strength of T300/69 laminates

Low-velocity Impact Damage Analysis in Composite Laminates

NUMERICAL FAILURE SIMULATION OF BOLT-LOADED COMPOSITE LAMINATE

EXPERIMENT STUDIES AND FEM SIMULATION OF REPAIRED COMPOSITE LAMINATES

Simulation and experimental studies of the repaired composite laminate

Numerical Simulation of Compression-After-Impact Process of Composite Laminates

EXPERIMENT AND MODELLING OF REPAIRED COMPOSITE LAMINA UNDER COMPRESSION

Experimental and Numerical Study on Bearing Failure of Countersunk Composite–composite and Composite–steel Joints

Impact Resistance of Thin Plain Woven Composite Laminates under High-velocity Small Mass Impact

Experimental Investigation of Low-velocity Impact and Residual Compressive Strength of Composites

Damage and residual compressive strength of multi-layer composite laminates after low velocity impact

Numerical Simulation of Low Velocity Impact Failure of CCF300 Carbon Fiber Laminate Based on ABAQUS

Predicting Post-Impact Compression Strength of Composite Laminates under Multiple Low-Velocity Impacts

An Experimental and Numerical Investigation on Low-Velocity Impact Damage and Compression-after-impact Behavior of Composite Laminates