Abstract:To develop an efficient and clean technique for comprehensively utilizing potassic syenite resources exposed in the Eastern Qinling to Dabie area of China, a series of experiments were performed using a typical K-feldspar powder as raw material, with focus on the hydrothermal stability of microcline in KOH-H2O solution, reaction principle of preparing potassium sulfate, as well as processing by-products from alumina and silica residue. Microcline was easily transformed into kalsilite by dislodging 2/3 SiO2 of the K-feldspar in the solution, resulting in nearly hundred percent higher concentration of K2O in the solid product, from which nearly pure solution of potassium sulfate was then obtained by dissolution with sulfuric acid, and further potassium sulfate was crystallized by evaporation of the solution or by the alcohol precipitation method. The alkaline solution of mainly potassium silicate reacted with lime milk to precipitate calcium silicate hydrate, from which needle-shaped wollastonite powder was synthesized hydrothermally, and then by calcination. The alumina and silica residue were used to make calcined kaolin first by acidic washing, and then by calcination. The whole procedure developed in this research was simple and economical, with recovery ratio of K2O up to 94.0%. In such a way, the components of K2O, Al2O3, and SiO2 in K-feldspar of the ores were wholly transformed to valuable products, giving rise to maximum utilization of K-feldspar resources, and also minimum consumption of relevant mineral resources. The technique is noted for energy conservation, high efficiency and clean production.

Kinetics of Hydrothermal Decomposition of Potassium Feldspar with Calcium Hydroxide

Hydrothermal Decomposition Process of K‐feldspar in NaOH Solution

K-Feldspar Decomposition Using CaO by Hydrothermal Method

REACTIVE MECHANISM OF POTASSIUM FELDSPAR DISSOLUTION UNDER HYDROTHERMAL CONDITION

Kinetic experiments on decompositionof K-feldspar with CaCl_2 and NaCl for extraction of potassium

Experimental Study on Synthesis of Tobermorite by Decomposing Potassium Feldspar

Hydrothermal decomposition of K-feldspar in KOH–NaOH–H 2 O medium

Hydrothermal reaction of K‐feldspar powder in NaOHCa (OH) 2 mixed medium

Hydrothermal reaction of K‐feldspar powder in NaOHCa (OH) <sub>2</sub> mixed medium

Experimental Study on Decomposition of K-feldspar with CaCl_2 and NaCl for Extraction of Potassium

THERMODYNAMIC ANALYSIS AND EXPERIMENTS OF THERMAL DECOMPOSITION FOR POTASSIUM FELDSPAR AT INTERMEDIATE TEMPERATURES

Synthesis of Tobermorite Nano-scale Powder from Potassium Feldspar:Reactive Mechanism Research

Leaching Process of Potassium Feldspar by Sub-Molten Salt at Low Temperature

Hydrothermal decomposition of glucose and fructose with inorganic and organic potassium salts.

Decomposition Kinetics Of Nano-Particle Calcite

Extraction of potassium from K-feldspar via the CaCl2 calcination route

Kinetics of Decomposition Reactions of Saima Nepheline Syenite by Hydrothermal Treatment with Sodium Hydroxide Solution

Hydrothermal processing on potassic syenite powder: Zeolite synthesis and potassium release kinetics

Thermodynamic Analysis on Decomposition reactions of Potassium Feldspar and Evaluation of the Processes

Preparation of potassium sulfate from K-feldspar by hydrothermal alkaline method:reaction principle and process evaluation

Synthesis of KAlSiO4 by Hydrothermal Processing on Biotite Syenite and Dissolution Reaction Kinetics