Abstract:The effects of processing parameters on deformation behavior of a new near 13 titanium alloy were investigated by using compression tests. The experiments were carried out in the Gleeble-3800 thermal and mechanical simulator in the temperature range of 770-970 degrees C and strain rate range of 10(-3)-10s(-1), and height direction reduction of 70%. The results show that the flow stress of Ti-7333 titanium alloy increases obviously with the strain and reaches a peak, then decreases to a steady value. The steady and peak stress significantly decreases with the increase of deformation temperature and decrease of strain rate. The flow stress model of Ti-7333 titanium alloy during high temperature deformation was established by using the regression method. The average relative difference between the calculated and experimental flow stress is 6.33%. The flow stress model can efficiently predict the deformation behavior of Ti-7333 titanium alloy during high temperature deformation.

High temperature deformation behavior of Ti-7333 titanium alloy and its flow stress model