Abstract:Antibiotic bioactive coatings containing Ca, P, Zn, 0 and Ti elements were prepared by means of a microarc oxidation technology （MAO） on pure titanium surfaces in an electrolytic solution of （NH4 ）2HPO4and （CH3 COO）2Ca·H20 as well as ZnO precursor. The oxide coatings were analyzed for surface morphology, cross section morphology and microstructure with SEM and XRD respectively. The surface roughness, bond strength and inhibition rate were also measured. The results show that the main crystalline phase on surface is TiO2 , and a small amount of zinc oxide and Ca-P salts exist in the coatings. Oxide coating consisting of compact inner layer and porous outer layer with micropore of 1-5μm in diameter is formed on the pure titanium after microarc oxidation treating. The surface roughness （Ra ） and bonding strength have significant increase and reach （1. 627±0.054）μm and （40.34±0. 014） MPa, respectively. At presence of zinc oxide, the inhibition rate of 90% indicate that the coating has a good antibacterial activity and it is beneficial to improve success rate of planting.

Antibiotic Bioactive Coatings on ,ti Surfaces by Microarc Oxidation Technology