Enhanced piezoelectric properties of 〈001〉 textured lead-free (K xNa 1-x) 0.946Li 0.054NbO 3 ceramics with large strain

Jigong Hao,Chenggen Ye,Bo Shen,Jiwei Zhai
DOI: https://doi.org/10.1002/pssa.201127747
2012-01-01
Abstract:Dense < 001 >-oriented (KxNa1-x)(0.946)Li0.054NbO3 (KxNLN) ceramics with high texture quality (Lotgering factor F001>80%) and excellent piezoelectric properties were produced by templated grain growth using plate-like NaNbO3 particles as templates. Compared with randomly oriented KxNLN ceramics, textured samples show greatly enhanced properties. The room-temperature strain hysteresis S, the piezoelectric coefficient d(33)* and d(33) reach up to 0.150.21%, 333-471pm/V, and 231-254pC/N, respectively, which are all about 1.61.8 times larger than those of nontextured ceramics with the same composition. The temperature-dependent strain characteristic is shown in both textured and nontextured ceramics around the polymorphic phase transition (PPT) temperature, confirming that this behavior is determined by the PPT temperature, which is unaffected by texturing. Moreover, good resistance to thermal depoling was obtained in KxNLN ceramics, indicating this system is a very promising piezoelectric material for high-temperature applications.
What problem does this paper attempt to address?