Abstract:Binary Mg–Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg–xCa (x=1–3 wt%) alloys were composed of two phases, α(Mg) and Mg2Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg–1Ca alloy (71.38±3.01MPa and 1.87±0.14%) were largely improved after hot rolling (166.7±3.01MPa and 3±0.78%) and hot extrusion (239.63±7.21MPa and 10.63±0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg–xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg2Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg–1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg–1Ca alloy extraction medium was better than that of control. Moreover, Mg–1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of osteoblast and osteocytes were observed around the Mg–1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg–1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)2 and hydroxyapatite formed on the surface of Mg–1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p>0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg–1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization.

In-vitro Cytotoxicity and In-Vivo Biocompatibility of As-Extruded Mg–4.0Zn–0.2Ca Alloy

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Preparation and characterization of a new biomedical Mg-Zn-Ca alloy

In Vitro and in Vivo Degradation Behavior of Mg–2Sr–Ca and Mg–2Sr–Zn Alloys

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity of Mg-4zn-3ha Alloy for Biodegradable Implant Materials

In vivo biodegradation and biocompatibility of Mg-Zn alloys

Biocompatibility of magnesium-zinc alloy in biodegradable orthopedic implants

In Vitro and Vivo Biocompatibility and Degradability of Low-Alloyed Mg-Zn-Ca-MgO Composite As Bone Repair Biomaterials

Evaluation of a New Mg–Zn–Ca–Y Alloy for Biomedical Application

In Vitro and in Vivo Investigation on Biodegradable Mg-Li-Ca Alloys for Bone Implant Application

In Vitro and In Vivo Analysis of the Mg-Ca-Zn Biodegradable Alloys

Development of New Medical Mg-Zn-Ca-Y Alloy and In-Vitro and In-Vivo Evaluations of Its Biological Characteristics

Evaluation on the corrosion resistance, antibacterial property and osteogenic activity of biodegradable Mg-Ca and Mg-Ca-Zn-Ag alloys

The Development of Binary Mg-Ca Alloys for Use As Biodegradable Materials Within Bone

In Vivobiocompatibility and Degradation Behavior of Mg Alloy Coated by Calcium Phosphate in a Rabbit Model

In vitro and in vivo assessment of the effect of biodegradable magnesium alloys on osteogenesis

In Vitro Effects of Mg-Zn Alloy on Proliferation, Differentiation and Mineralization in MC3T3-E1 Cells

In Vitro and in Vivo Studies on A Mg-Li-X Alloy System Developed As A New Kind of Biological Metal

Cytotoxicity and hemolytic properties of biodegradable Mg-Zn alloy

Corrosion Resistance and Biocompatibility Assessment of a Biodegradable Hydrothermal-Coated Mg-Zn-Ca Alloy: An in Vitro and in Vivo Study