Abstract:Carbon coated hollow alpha-Fe2O3 spheres were prepared via a facile two-step hydrothermal method. The appearance and crystalline structure of the samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The morphology showed that the hollow spheres were composed of well crystallized nanoparticles after the first hydrothermal reaction and subsequent calcinations. A thin carbon film was coated on each Fe2O3 nanoparticles after the second hydrothermal procedure. This carbon coating was probably beneficial to maintain the microstructure of the active material during repeatable lithiation and delithiation. Afterwards, the samples were assembled into half-cells to investigate the electrochemical properties. The electrode delivered relatively high initial discharge/charge capacities of 1291/890 mA h g(-1) at the rate of 0.3 C. The reversible capacity maintained very well in a prolonged 140 cycles. The capacity retention was 89% after 70 cycles, and that was 81% after 140 cycles. This exceptional lithium storage property was probably attributed to the porous and hollow structure which allowed the penetration of electrolyte to the inner of the electrode, the nanoscale Fe2O3 particles which shortened the migration pathway for lithium ion, and the carbon coating which kept the active materials structure intact. The attractive electrochemical performance suggested the carbon coated hollow Fe2O3 spheres would be the potential anode material for future lithium ion battery.

Fe3O4C Open Hollow Sphere Assembled by Nanocrystals and Its Application in Lithium Ion Battery

Synthesis and Characterization of Hollow Alpha-Fe2o3 Spheres with Carbon Coating for Li-Ion Battery

Uniform hollow Fe 3 O 4 spheres prepared by template-free solvothermal method as anode material for lithium-ion batteries

Green Fabrication of Sandwich-Like and Dodecahedral C@Fe3O4@C As High-Performance Anode for Lithium-Ion Batteries

Facile Synthesis of Fe3S4hollow Spheres with High-Performance for Lithium-Ion Batteries and Water Treatment

α-Fe2O3 hollow microspheres assembled by ultra-thin nanoflakes exposed with (241) high-index facet: Solvothermal synthesis, lithium storage performance, and superparamagnetic property

High-performance lithium-ion batteries with different hollow-degree Fe3O4@C hollow nanostructures

Cobalt oxide hollow microspheres with micro- and nano-scale composite structure: Fabrication and electrochemical performance

Fe3O4 Submicron Spheroids As Anode Materials for Lithium-Ion Batteries with Stable and High Electrochemical Performance

Hierarchical Fe3O4@C Nanospheres Derived from Fe2O3/MIL-100(Fe) with Superior High-Rate Lithium Storage Performance

Synthesis of Hierarchical Hollow-Structured Single-Crystalline Magnetite (fe3o4) Microspheres: the Highly Powerful Storage Versus Lithium As an Anode for Lithium Ion Batteries

An Fe3O4–FeO–Fe@C Composite and Its Application As Anode for Lithium-Ion Battery

Carbon-coated MnFe2O4 nanoparticle hollow microspheres as high-performance anode for lithium-ion batteries

Fe3O4 Hollow Nanospheres Grown In Situ in Three-Dimensional Honeycomb Macroporous Carbon Boost Long-Life and High-Rate Lithium Ion Storage

Fe3O4/Fe/carbon Composite and Its Application As Anode Material for Lithium-Ion Batteries.

Lysine-assisted hydrothermal synthesis of hierarchically porous Fe 2O3 microspheres as anode materials for lithium-ion batteries

Hollow CuFe2O4 spheres encapsulated in carbon shells as an anode material for rechargeable lithium-ion batteries

Controllable Synthesis of Hollow MnFe2O4 by Self-Etching and Its Application in High-Performance Anode for Lithium-Ion Batteries

Facile Synthesis of Hierarchically Porous Li4Ti5O12 Microspheres for High Rate Lithium Ion Batteries

3-Dimensional Hierarchically Porous ZnFe2O4/C Composites with Stable Performance As Anode Materials for Li-ion Batteries

Formation of Uniform Fe3O4 Hollow Spheres Organized by Ultrathin Nanosheets and Their Excellent Lithium Storage Properties