Abstract:The thermodynamic analysis of bottom-blown direct reduction of lead sulfate with carbon was studied in this investigation, and the industrial verification test was carried out. The thermodynamic analysis results indicated that lead sulfate was easily decomposed into lead sulfide at PSO2\documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$P_{{{\text{SO}}_{2} }}$$\end{document} values above 10−3 atm and PO2\documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$P_{{{\text{O}}_{2} }}$$\end{document} values below 10−12 atm. The lead sulfide could be converted into lead oxide or metallic lead in the decomposition of lead sulfate by the addition of Fe, FeS and CaO. The phase diagrams for the C–CaO–PbSO4 and C–Fe–PbSO4 systems were constructed at 1273–1573 K, indicating that the addition of coal, limestone and scrap iron during reduction could cause the slag chemical composition variation, which consequently changed the Pb-liq + CaS and Pb-liq + FeS zones area. The industrial verification test demonstrated that the average addition of limestone, scrap iron and coal in the direct reduction of lead paste was approximately 2.8%, 5.4% and 11.5%, respectively. The direct recovery rate of lead bullion was about 61%, and the total recovery rate of lead could reach 99%. The average content of lead, zinc and sulfur in the reduced slag was 2.42%, 1.55% and 0.51%, respectively.

Desulfurization and structural transformation behavior of lead sulfate in sodium hydroxide molten salt

Batch Production of Lead Sulfate from Spent Lead-Acid Batteries<i> via</i> an Oxygen-Free Roasting Route: A Negative-Carbon Strategy

Preparation of High Purity Lead Oxide from Spent Lead Acid Batteries via Desulfurization and Recrystallization in Sodium Hydroxide

Batch Production of Lead Sulfate from Spent Lead–Acid Batteries via an Oxygen-Free Roasting Route: A Negative-Carbon Strategy

Molten salt mediated low-temperature direct roasting of spent lead paste

Hydrothermal desulfurization of spent lead paste based on comproportionation reaction

From Lead Paste to High-Value Nanolead Sulfide Products: A New Application of Mechanochemistry in the Recycling of Spent Lead–Acid Batteries

Primary study on synthesis of PPFS and its application for depositing lead from wastewater

Recovery of lead from lead paste in spent lead acid battery by hydrometallurgical desulfurization and vacuum thermal reduction

Thermodynamic analysis of the bottom-blown direct reduction of lead sulfate with carbon

Electrochemical behavior and electrolytic preparation of lead in eutectic NaCl−KCl melts

An innovative synergistic recycling route of spent lead paste and lead grid based on sodium nitrate reuse

An environment-friendly strategy for recovery of α-PbO from spent lead paste: Based on the thermochemical reduction of PbO 2 with ammonium sulfate

Pollution-free Recycling of Lead and Sulfur from Spent Lead-Acid Batteries Via a Facile Vacuum Roasting Route

Ultrasonic-Assisted Synthesis of Lead Citrate as Precursor for Preparation of Lead Oxide from Lead Sulfate

Transformation process of cathode lead structure in the recovery of waste lead paste by suspension electrolysis

Directly Recovering Lead and Recycling Electrolyte via Electrolyzing Desulfurized Lead Paste with PVDF as Binder

Separation of sodium sulfate from high-salt wastewater of lead-acid batteries

Analysis of a more sustainable method for recycling waste lead batteries: Surface renewal promotes desulfurization agent regeneration

Selective preparation of lithium carbonate from overhaul slag by high temperature sulfuric acid roasting - Water leaching

The Role of PbO2 in the Metal Lead Recovery from Lead Paste Via Suspension Electrolysis with Sulfuric Acid as Electrolyte