Effect of sputtering gold coating on the bonding strength between pure titanium and two low-fusing porcelains
Liang Rong,Xiaoping Luo,Ning Li,Zhigang Xie,Zhi Li,Xianzhi Shen
DOI: https://doi.org/10.11752/j.kqcl.2018.01.02
2018-01-01
Abstract:Objective To study the effect of sputtering gold coating on the bonding strength between pure titanium and two low-fusing porcelains according to the protocol of ISO 9693,and to characterize the titaniumporcelain interfaces.Methods Forty machined pure titanium samples were prepared according to the ISO 9693 protocol.Based on the type of sintering porcelains (SP:Super Porcelain Ti-22;TC:Triceram) and titanium base with or without sputtering gold (Au),forty titanium samples were divided equally into four groups (AuSP,AuTC,SP and TC group).Low-fusion dental porcelain was then sintered onto the titanium samples.Three-point bending test was performed to assess the bonding strength,and optical stereomicroscope was used to characterize the titanium-porcelain adhesion and determine the failure mode.The titanium-ceramic interface was examined by Field Emission Scanning Electron Microscope (FE-SEM) and Electron Micoporbe Analysis (EMPA).Results The bonding strength of the AuSP groups was much higher than that of the SP groups (P＜0.05),while no significant difference was found between AuTC group and TC group (P＞005).The SP,AuTC and TC groups showed predominately adhesive fracture,whereas the failure mode of AuTC group was mixture of cohesive and adhesive,mainly cohesive.FE-SEM with EMPA did not show visible cracks in the Au groups.The depth of titanium and oxygen diffusion was decreased in the presence of the gold coating.Conclusions Sputtering gold intermediate coatings can inhibit titanium and oxygen diffusion,improve the bonding strength between Super Porcelain Ti-22 system,but does not affect the bonding strength of Porcelain Triceram system.