Fabrication and evaluation of polyamide 6 composites with electrospun polyimide nanofibers as skeletal framework

Yujen Chen,Donghua Han,Wen Ouyang,Shuiliang Chen,Haoqing Hou,Yong Zhao,Hao Fong

DOI: https://doi.org/10.1016/j.compositesb.2011.11.071

2012-01-01

Abstract:In this study, two types of polyimide (PI) nanofiber mats, including (1) the mats consisting of (almost) randomly overlaid PI nanofibers and (2) the mats consisting of highly aligned PI nanofibers, were prepared by the materials-processing technique of electrospinning. The nanofiber mats were subsequently used to develop composites with polyamide 6 (PA6) via the composites – fabrication method of polymer melt infiltration lamination (PMIL). Owing to superior mechanical properties (i.e., the tensile strength and modulus were 1.7GPa and 37.0GPa, respectively) and large specific surface area of electrospun PI nanofibers, the PI/PA6 composites with PI nanofiber mats as skeletal framework demonstrated excellent mechanical properties. In particular, the PI/PA6 composite containing 50wt.% of aligned PI nanofibers had the tensile strength and modulus of 447MPa and 3.0GPa along the longitudinal direction, representing ∼700% and ∼500% improvements as compared to neat PA6.